The steel plates for testing obtained a clean and fresh surface after degreasing by alkali and acidity and to be protested from reoxidation by being dipped into liquid wax. The results after hot dipping experiments in lab. showed that a complete aluminized coat with a good property could be obtained under a condition of hot-dipping temperature at about 730 ℃, hot -dipping time at about 2 minutes. It was found that the transition layer was mainly composed of Fe2 Al5 intermetallic compound by SEM (Scanning Electronic Microscope) observation. Effects of elements copper and titanium in aluminum coating on adherence quality, corrosion resistance performance and thickness of the transition layer were investigated, the following results were drawn: The adherence quality is strongly enhancedby copper element and gives the best performance at the 2% mass percent content of copper, while it is almost indifferent with titanium content. The corrosion resistance property is enhanced by titanium and is deteriorated by copper, when the mass percent content of titaniumis 0.3% , the coating exhibits the best anti-corrosion performance. At present condition, both copper and titanium make transition layer thinner.