在低温反应条件下,通过超声的方法,以DBS作为表面活性剂,制备了ZnO纳米棒.化学反应的低温条件由冰水浴提供,温度为0～5℃.扫描电子显微镜和光学显微镜观察表明,所制备的纳米棒形状均一,截面为六方型,直径100nm,长度1μm;X射线衍射表征指出所得到的纳米棒为六方晶型.同时,我们也研究了反应温度、表面活性剂含量、超声、回流时间对ZnO纳米棒形貌的影响.与其它制备方法相比,低温与超声技术可以更为方便获得分布均一,长径比较小的ZnO纳米棒.
参考文献
| [1] | Zhao Qitao;Hou Li-song.[J].Inorganic Chem Commu,2003(06):971-973. |
| [2] | Huang Chin-Hsien;Whang Wha-Tzong .[J].Materials Chemistry and Physics,2003,82:705-710. |
| [3] | Zheng MJ.;Zhang LD.;Li GH.;Shen WZ. .Fabrication and optical properties of large-scale uniform zinc oxide nanowire arrays by one-step electrochemical deposition technique[J].Chemical Physics Letters,2002(1/2):123-128. |
| [4] | Huang M H;Wu Y et al.[J].Advanced Materials,2001,13:113-116. |
| [5] | Pan Z W;Dai Z R;Wang Z L .[J].Science,2001,291:1947-1949. |
| [6] | Yao B D;Chan Y F et al.[J].Applied Physics Letters,81:757-759. |
| [7] | Kong Y C;Li Q K et al.[J].Applied Physics Letters,78:407-409. |
| [8] | Huang M H;Mao S et al.[J].Science,2001,292:1897-1899. |
| [9] | Liu Bin;Zeng Hua Chun .[J].Journal of the American Chemical Society,2003,125:4430-4431. |
| [10] | Guo Lin;Ji Yun Liang et al.[J].Journal of the American Chemical Society,2002,124:14864-14865. |
| [11] | 姜国华,姜继森.金属氧化物纳米线和纳米棒的制备及应用[J].材料科学与工程学报,2003(05):753-758. |
| [12] | 宋旭春,徐铸德,陈卫祥,韩贵,刘波,郑遗凡.氧化锌纳米棒的制备和生长机理研究[J].无机化学学报,2004(02):186-190. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%