在Gleeble?1500热/力模拟机上,对Mg-10Gd-4.8Y-0.6Zr镁合金进行高温压缩试验,压缩时设定应变速率范围为0.001~1 s?1,温度范围为623~773 K,最大真应变为1.3;研究该合金高温变形时流变应力与应变速率、变形温度之间的关系及变形过程中的微观组织演化;计算塑性变形表观激活能及相应的应力指数;建立该合金的加工图.结果表明:在该合金的加工图中,功率耗散系数η随应变速率的降低及温度的升高而不断增加,失稳区域随应变量的增加而扩大;综合得出该合金的最佳实际变形工艺为温度723~773 K、应变速率0.1~1 s?1.
@@@@The processing parameters of Mg-10Gd-4.8Y-0.6Zr magnesium alloy were investigated. The tests were carried out in the strain rate range of 0.001?1 s?1 and temperature range of 623?773 K, and with the maximum true strain of 1.3 on hot-simulation machine Gleeble?1500. The relationships among the flow stress, the strain rate and the temperature as well as microstructure evolution were investigated. The apparent activation energy during plastic deformation and corresponding stress index were calculated, the processing maps were drawn. The test reveals that the efficiency of power dissipation increases with the increase of temperature and the decline of strain rate, and the instability region expands due to the rise of the temperature in processing maps. Optimal processing parameters were the temperature range of 723?773 K and the strain rate range of 0.1?1 s?1.
参考文献
| [1] | Mordike BL. .Creep-resistant magnesium alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1-2 Special Issue SI):103-112. |
| [2] | MARUYAMA K;SUZUKI M;SATO H .Creep strength of magneium-based alloys[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2002,33(03):875-882. |
| [3] | Ifeanyi Anthony Anyanwu;Shigeharu Kamado;Yo Kojima .Aging Characteristics and High Temperature Tensile Properties of Mg-Gd-Y-Zr Alloys[J].Materials transactions,2001(7):1206-1211. |
| [4] | 夏长清,武文花,吴安如,王银娜.Mg-Nd-Zn-Zr稀土镁合金的热变形行为[J].中国有色金属学报,2004(11):1810-1816. |
| [5] | 郭强,严红革,陈振华,张辉.AZ31镁合金高温热压缩变形特性[J].中国有色金属学报,2005(06):900-906. |
| [6] | Li, L.;Zhang, X. .Hot compression deformation behavior and processing parameters of a cast Mg-Gd-Y-Zr alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2011(3):1396-1401. |
| [7] | 刘楚明,刘子娟,朱秀荣,周海涛.镁及镁合金动态再结晶研究进展[J].中国有色金属学报,2006(01):1-12. |
| [8] | A. GALIYEV;R. KAIBYSHEV;G. GOTTSTEIN .CORRELATION OF PLASTIC DEFORMATION AND DYNAMIC RECRYSTALLIZATION IN MAGNESIUM ALLOY ZK60[J].Acta materialia,2001(7):1199-1207. |
| [9] | J.C. Tan;M.J. Tan .Dynamic continuous recrystallization characteristics in two stage deformation of Mg-3Al-1Zn alloy sheet[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):124-132. |
| [10] | POIRIER J P;关德村.晶体的高温塑性变形[M].大连:大连理工出版社,1989:1. |
| [11] | 余琨,黎文献,王日初,马正青,赵俊,孟力平.Mg-5.6Zn-0.7Zr-0.8Nd合金高温塑性变形的热/力模拟研究[J].金属学报,2003(05):492-498. |
| [12] | Prasad, YVRK;Rao, KP;Hort, N;Kainer, KU .Optimum parameters and rate-controlling mechanisms for hot working of extruded Mg-3Sn-1Ca alloy[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2009(1/2):25-31. |
| [13] | Wang CY;Wang XJ;Chang H;Wu K;Zheng MY .Processing maps for hot working of ZK60 magnesium alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1-2):52-58. |
| [14] | O. Sivakesavam;Y.V.R.K. Prasad .Hot deformation behaviour of as-cast Mg-2Zn-1Mn alloy in compression: a study with processing map[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):118-124. |
| [15] | ZIEGLER H.An introduction to thermomechanics[M].Amsterdam,New York,Oxford:North-holland Publishing Company,1983 |
| [16] | 刘娟,崔振山,李从心.镁合金ZK60的三维加工图及失稳分析[J].中国有色金属学报,2008(06):1020-1026. |
| [17] | KUBOTA K;MABUCHI M;HIGASHI K .Review processing and mechanical properties of fine-grained magnesium alloy[J].Journal of Materials Science,1999,34(10):4311-4320. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%