用化学处理法制备了片状TiO2微粒,并对片状TiO2微粒及其焙烧产物的形貌和物相进行了分析.结果发现:片状TiO2微粒为无定型结构,片状颗粒非常薄;当加热到300℃以上时,TiO2片收缩变厚并由无定型转变为锐钛矿型结构,当继续加热使片状TiO2微粒由锐钛矿转变为金红石型结构时,原来的片状TiO2部分转变为长棒状的金红石型晶柱结构,而原料TiO2无论在多高的温度下焙烧都未出现长棒状晶柱结构;片状TiO2微粒的A→R相变温度比原料低大约300℃.
参考文献
| [1] | 罗瑾,周静,祖延兵,林仲华.电沉积二氧化钛纳米微粒膜的光电化学性能和表面形貌研究[J].高等学校化学学报,1998(09):1484-1487. |
| [2] | Bach U.;Lupo D.;Comte P.;Moser JE.;Weissortel F.;Salbeck J. .Solid-state dye-sensitized mesoporous TiO2 solar cells with highphoton-to-electron conversion efficiencies[J].Nature,1998(6702):583-585. |
| [3] | Birkefeld L D;Azad A M;Akbor S A .[J].Journal of the American Ceramic Society,1992,75:2964. |
| [4] | Fukushima K;Yamada I .[J].Journal of Applied Physics,1989,65:619. |
| [5] | Vinodgopal K;Bedja I;Kamat P V .[J].Chemistry of Materials,1996,8:2180. |
| [6] | Zhou B S;Xiao L Z;Li T J et al.[J].Applied Physics Letters,1991,59:1826. |
| [7] | Fox M A;Dulay M T .[J].Chemical Reviews,1993,93:341. |
| [8] | Hoffman M R;Martin S T;Chuiet W .[J].Chemical Reviews,1995,95:69. |
| [9] | 李芳柏;古国榜;李新军 等.[J].物理化学学报,2001,17(01):37. |
| [10] | Yamashita H;Kawasaki S;Ichihashi Y et al.[J].Journal of Physical Chemistry B,1998,102:5870. |
| [11] | 张玉红,熊国兴,杨维慎,傅贤智.溶胶- 凝胶法制备复合 MxOy-TiO2光催化剂[J].物理化学学报,2001(03):273-277. |
| [12] | 周幸福,褚道葆,韩爱杰,顾家山,林昌健,田中群,谭建光.电化学溶解钛金属直接水解法制备纳米TiO2[J].物理化学学报,2001(04):367-371. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%