采用低温反应自熔新工艺,由经过预氧化的Mg粉原位合成了MgO颗粒增强镁基复合材料,并对其显微组织和力学性能进行了检测.结果表明:低温反应自熔时,因Mg颗粒处于全熔或半熔状态,表面的氧化膜得到了有效地破碎、细化,并在液相熔蚀和自身表面张力的共同作用下,球化成微米和亚微米级MgO颗粒;形成的MgO颗粒不但与基体结合良好、分散均匀,而且因具有很高的强度和刚度,对基体产生了较好的增强效果.与粉末冶金法相比,采用低温反应自熔法制备的镁基复合材料的组织和性能均显示出明显优势.
参考文献
| [1] | Chua B W;Lu L .[J].Computers & Structures,1999,47:595. |
| [2] | Zheng MY.;Wu K.;Kamado S.;Kojima Y. .Aging behavior of squeeze cast SiCw/AZ91 magnesium matrix composite[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):67-75. |
| [3] | 郗雨林,柴东朗,张文兴,席生歧,周敬恩.粉末冶金法制备SiC晶须增强MB15镁基复合材料[J].稀有金属材料与工程,2005(07):1131-1134. |
| [4] | Jiang Q C;Li X L;Wang H Y .[J].Scripta Materialia,2003,48:713. |
| [5] | Ho K F;Gupta M;Srivatsan T S .[J].Materials Science and Engineering A-structural Materials Properties Microstructure and Processing,2004,369:302. |
| [6] | Hassan S F;Gupta M .[J].Journal of Alloys and Compounds,2002,335:10. |
| [7] | Perez P;Garces G;Adeva P .[J].Computer Science & Technology,2004,64:145. |
| [8] | Hassan S F;Gupta M .[J].Journal of Alloys and Compounds,2002,345:246. |
| [9] | Xi Y L;Chai D L;Zhang W X et al.[J].Materials Letters,2005,59:1831. |
| [10] | 郗雨林,柴东朗,张文兴,曹利强.低温反应自熔制备Mg基复合材料的组织与性能[J].热加工工艺,2005(05):7-10. |
| [11] | 虞觉奇.二元合金状态图集[M].上海:上海科学技术出版社,1987:245. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%