以Li_3N和BBr3为原料,采用溶剂热法在220 ℃合成了h-BN纳米晶,研究了反应时间、表面活性剂和诱导晶粒对产物的影响.研究结果表明:反应产物主要为h-BN,同时含有少量c-BN,随着反应时间从12 h延长至36 h,晶粒尺寸从20 nm增大至80 nm;十二烷基苯磺酸钠的引入可以控制产物颗粒尺寸在10 nm左右,并且使球形度得到提高;以h-AlN为诱导晶粒时,产物中六方相含量增加,并且出现了h-BN纳米棒.
Hexagonal boron nitride nanocrystals were prepared by solvothermal method at 220 ℃ using Li_3N and BBr3 as raw materials. The effects of reaction time, surfactant and induced seeds on the production waere studied. The experimental results indicate that the hexagonal boron nitride was the dominant production and cubic boron nitride could be also found. The size of the crystals grew from 20 nm to 80 nm as the reaction time extended from 12 h to 36 h. With the addition of surfactant, the crystal size could be limited to 10 nm and the degree of sphericity improved. The content of hexagonal phase increased with the addition of h-AlN seeds, and some rod like h-BN nanocrystals appeared in the production.
参考文献
| [1] | 崔得良;郝霄鹏;徐现刚 等.制备氮化硼纳米微粉的方法[P].中国专利:CN1101337C,2003-2-12. |
| [2] | San Hua Lim;Jizhong Luo;Wei Ji .Synthesis of boron nitride nanotubes and its hydrogen uptake[J].Catalysis Today,2007(3/4):346-350. |
| [3] | 李剑锋,姚连增,蔡维理,牟季美.氮化硼包覆纳米氧化锌体系的 光致发光特性研究[J].物理学报,2001(08):1623-1626. |
| [4] | 陈坤,袁颂东.氮化硼球形纳米粒子的制备及影响因素分析[J].武汉理工大学学报,2006(08):9-11,19. |
| [5] | Bernard S;Chassagneux F;Berthet M P et al.Structure and Mechanical Properties of a High-performance BN Fibre[J].Journal of the European Ceramic Society,2002,22:2047-2059. |
| [6] | 胡婉莹.连续合成六方氮化硼的新工艺[J].现代技术陶瓷,2002(02):35-36,47. |
| [7] | LI Kai,JIANG HaiHui,LIAN Gang,WANG QiLong,ZHAO Xian,CUI DeLiang,TAO XuTang.Investigation on the key factors in the hydrothermal synthesis of BN: The way of introducing sodium azide[J].科学通报（英文版）,2007(13):1785-1790. |
| [8] | Shouyi Dong;Xiaopeng Hao;Xiangang Xu .The effect of reactants on the benzene thermal synthesis of BN[J].Materials Letters,2004(22/23):2791-2794. |
| [9] | Wang S B;Xu X W;Fan H L et al.Low Pressure Synthesis of Boron Nitride with (C2H5)2O@BF3 and Li_3N Precursor[J].Journal CSUT,2005,12(01):60-63. |
| [10] | Hao X P;Cui D L;Shi G X et al.Synthesis of Cubic Boron Nitride at Low-pressure Conditions[J].CHEMISTRY OF MATERIALS,2001,13(08):2457-2459. |
| [11] | 牟其勇,徐晓伟,范慧俐,鲍俊萍,李玉萍,信春雨.Li3N在合成BN反应中的作用研究[J].人工晶体学报,2004(01):40-42. |
| [12] | 毛培坤.表面活性剂产品工业分析[M].北京:化学工业出版社,2003:138-141. |
| [13] | 董守义,郝霄鹏,于美燕,李凯,王琪珑,蒋民华,崔得良.GaP纳米晶对溶剂热合成氮化硼的物相和微观形貌的影响[J].功能材料,2004(06):695-697. |
| [14] | 施尔畏;陈之战;元如林.水热结晶学[M].北京:科学出版社,2004:229-231. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%