HAZ CRACKING AND HOT DUCTILITY OF Ni_3AI CONTAINING Zr ALLOY

B. N. Qian , J. L. Li , J. T. Guo and B. Z. Wei (1)Institute of Metal Research , The Chinese Academy of Sciences , Shenyang 110015 , China 2)Shanghai University , Shanghai 200072 , China)

Keywords： Ni_3Al bearing Zr alloy , null , null

The HAZ cracking test in EB welding condition and hot ductility test show that the cracking mechanism is the formation of Ni - Ni5Zr eutectic which is resulting from the enrichment of Zr in grain boundaries during welding.In order to eliminate HAZ cracks the diffusion and recrystalization anealing treatment after cast and during cold rolling should be conducted in vacuum or protecting atmosphere and at the same time a slow welding speed is necessary.

参考文献

[1]

上一张下一张

PDF下载
导出引用
下载XML
收藏文章

计量

下载量()
访问量()

作者相关

在本站搜索
B. N. Qian J. L. Li J. T. Guo and B. Z. Wei (1)Institute of Metal Research The Chinese Academy of Sciences Shenyang 110015 China 2)Shanghai University Shanghai 200072 China)
在百度学术搜索
B. N. Qian J. L. Li J. T. Guo and B. Z. Wei (1)Institute of Metal Research The Chinese Academy of Sciences Shenyang 110015 China 2)Shanghai University Shanghai 200072 China)
在万方数据库搜索
B. N. Qian J. L. Li J. T. Guo and B. Z. Wei (1)Institute of Metal Research The Chinese Academy of Sciences Shenyang 110015 China 2)Shanghai University Shanghai 200072 China)
在CNKI搜索
B. N. Qian J. L. Li J. T. Guo and B. Z. Wei (1)Institute of Metal Research The Chinese Academy of Sciences Shenyang 110015 China 2)Shanghai University Shanghai 200072 China)

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

HAZ CRACKING AND HOT DUCTILITY OF Ni_3AI CONTAINING Zr ALLOY

参考文献