为了研究锂离子电池的正极材料LiCoO2的新型制备方法,考查了反应原料配比、微波输出功率、微波合成温度和微波加热时间对LiCoO2结构和性能的影响.以LiOH·H2O和Co2O3为反应原料的最佳合成条件:Li/Co摩尔比为1.05:1,微波输出功率为360 W,反应时间为14 min,合成温度为800 ℃.所合成LiCoO2样品均采用XRD和SEM进行表征,结果表明,采用微波合成的LiCoO2样品为单一相层状结构且晶体结构发育良好;样品的充放电循环性能良好,首次循环放电容量为130 mAh/g.
参考文献
| [1] | 张凤敏,李宁,黎德育,张翠芬.锂离子电池正极材料研究现状[J].电池,2003(06):392-394. |
| [2] | 周燕芳,钟辉.锂离子电池正极材料的研究进展[J].材料开发与应用,2003(02):34-38,42. |
| [3] | B. Huang;Y-I. Jang;Y-M. Chiang;D. R. Sadoway .Electrochemical evaluation of LiCoO_2 synthesized by decomposition and intercalation of hydroxides for lithium-ion battery applications[J].Journal of Applied Electrochemistry,1998(12):1365-1369. |
| [4] | Fujitru S.;Ikegami M. .Sintering of Partially Stabilized Zirconia by Microwave Heating UsinG ZnO-MnO_2-A1_2o_3 Plates in a Domestic Microwave Oven[J].Journal of the American Ceramic Society,2000(8):2085-2087. |
| [5] | Yan HW.;Li H.;Chen LQ.;Huang XJ. .Electrochemical study on LiCoO2 synthesized by microwave energy[J].Solid state ionics,1998(Special Issue SI):11-15. |
| [6] | 李乃军,翟秀静,翟玉春,高虹.锂离子电池正极材料镍酸锂的合成[J].材料科学与工艺,2000(02):79-82. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%