根据电沉积磷灰石陶瓷技术,通过在含有Ca(NO3)2·4H2O、NH4H2PO4、NaNO3及H2O2的电解液中加入不同浓度的氟化钠作为引氟剂,在钛片表面进行电化学沉积,分别采用扫描电镜(SEM)、X射线衍射(XRD)、傅立叶变换红外光谱(FT-IR)、X射线光电子能谱(XPS)对所得涂层的表面形貌和理化性质进行分析.结果表明,通过上述方法可以在钛表面制备纳米晶含氟羟基磷灰石(FHA)涂层,涂层的含氟量与电解液中加入NaF的浓度有关.当NaF浓度低于0.012 mol/L时,随着引氟量的增加,所得FHA涂层的含氟量也相应增加;当NaF浓度高于0.012 mol/L后,涂层的含氟量不发生明显变化.
参考文献
| [1] | 左友松,刘榕芳,肖秀峰.电沉积HA/Ti复合涂层的研究[J].电镀与涂饰,2003(04):1-4. |
| [2] | E. Landi;G. Celotti;G. Logroscino .Carbonated hydroxyapatite as bone substitute[J].Journal of the European Ceramic Society,2003(15):2931-2937. |
| [3] | SHIRKHANZADEH M .Calcium phosphate coatings prepared by electrocrystallization from aqueous electrolytes[J].Journal of Materials Science: Materials in Medicine,1995,6(02):90-93. |
| [4] | Kim HW;Kong YM;Bae CJ;Noh YJ;Kim HE .Sol-gel derived fluor-hydroxyapatite biocoatings on zirconia substrate.[J].Biomaterials,2004(15):2919-2926. |
| [5] | Wang J;Chao Y;Wan Q .Fluoridated hydroxyapatite coatings on titanium obtained by electrochemical deposition.[J].Acta biomaterialia,2009(5):1798-1807. |
| [6] | Towler MR.;Best SM.;Gibson IR. .Novel processing of hydroxyapatite-zirconia composites using nano-sized particles[J].Journal of Materials Science Letters,2000(24):2209-2211. |
| [7] | Tanaka H.;Yasukawa A.;Kandori K.;Ishikawa T. .Surface structure and properties of fluoridated calcium hydroxyapatite[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2002(1/3):251-259. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%