目前对于水在防腐蚀涂层中的传输研究大都集中在静态浸泡条件下,且大部分都基于有机溶剂涂层,鲜见流速对无溶剂涂层在海水中传输行为的影响研究.在60℃的3.5％NaCl溶液中以3种无溶剂环氧防腐蚀涂层自由膜为研究对象,利用称重法(GM)研究了不同流速下水在涂层中的扩散行为,采用差示扫描量热法(DSC)和近红外光谱技术(NIR)研究了水的存在形式以及不同类型水的含量变化.结果表明:胺类固化环氧粉末涂层和酚醛固化环氧粉末涂层在试验流速范围内、酚醛胺固化无溶剂环氧液体涂层在较低流速范围内,水在涂层中的扩散符合FickⅡ模型,而在4 m/s的高流速下,水在无溶剂环氧液体涂层中的扩散偏离FickⅡ模型;随着流体流速增加,3种涂层自由膜的饱和吸水量增加,水在涂层自由膜中的扩散系数变大,涂层自由膜吸水达到饱和的时间减少;水在无溶剂环氧涂层自由膜中有3种存在形式:不形成氢键的水分子(S0)、形成1个氢键的水分子(S1)和形成2个氢键的水分子(S2).随着流速的增加2种环氧粉末涂层自由膜中S0、S1和S2的含量均增加,水对自由膜的塑化作用增强;而无溶剂环氧液体涂层由于水分子同未反应的环氧基团发生开环反应,使高分子链进一步地交联,导致自由膜内水分含量反而减小.
参考文献
| [1] | 林海潮;李谋成.涂层下金属的腐蚀过程[J].腐蚀科学与防护技术,2002(3):180-181. |
| [2] | Taylor, S.R.;Contu, F.;Santhanam, R.;Suwanna, P..The use of cationic fluoroprobes to characterize ionic pathways in organic coatings[J].Progress in Organic Coatings: An International Review Journal,20122/3(2/3):169-172. |
| [3] | Flavio Deflorian;Stefano Rossi.An EIS study of ion diffusion through organic coatings[J].Electrochimica Acta,20068/9(8/9):1736-1744. |
| [4] | 杨海;陆卫中;李京;张立新.一种环氧粉末涂层的吸水性研究[J].腐蚀科学与防护技术,2014(5):420-424. |
| [5] | 胡吉明;张鉴清;谢德明;曹楚南.水在有机涂层中的传输Ⅰ Fick扩散过程[J].中国腐蚀与防护学报,2002(5):311-315. |
| [6] | Jiming Zhou;James P. Lucas.Hygrothermal effects of epoxy resin. Part I: the nature of water in epoxy[J].Polymer: The International Journal for the Science and Technology of Polymers,199920(20):5505-5512. |
| [7] | Pellegrino Musto;Giuseppe Ragosta;Leno Mascia.Vibrational Spectroscopy Evidence for the Dual Nature of Water Sorbed into Epoxy Resins[J].Chemistry of Materials,20005(5):1331-1341. |
| [8] | Salvatore Cotugno;Giuseppe Mensitieri;Pellegrino Musto;Luigi Sanguigno.Molecular Interactions in and Transport Properties of Densely Cross-Linked Networks:A Time-Resolved FT-IR Spectroscopy Investigation of the Epoxy/H_2O System[J].Macromolecules,20053(3):801-811. |
| [9] | Jin, Y.;Wang, W.;Su, Z..Spectroscopic study on water diffusion in poly(l-lactide)-poly(ethylene glycol) diblock copolymer film[J].Macromolecules,20117(7):2132-2139. |
| [10] | Pethrick RA.;Mcewan I.;Mackinnon AJ.;Hayward D.;Cannon LA.;Jenkins SD.;Mcgrail PT.;Hollins EA..DIELECTRIC, MECHANICAL AND STRUCTURAL, AND WATER ABSORPTION PROPERTIES OF A THERMOPLASTIC-MODIFIED EPOXY RESIN - POLY(ETHER SULFONE)-AMINE CURED EPOXY RESIN[J].Macromolecules,199615(15):5208-5214. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%