以有机电致发光材料-8-羟基喹啉铝(Alq3)为研究对象,在其表面包覆SiO2来改善有机电致发光器件中的材料界面,从而延长器件寿命.利用透射电子显微镜、光致发光光谱、热重分析分别对产物的形貌、发光性能和热稳定性进行了表征,借助扫描电镜和X射线光电子能谱仪对产物的薄膜进行了微观分析,分别以Alq3和包覆了SiO2的Alq3为发光层制备了双层结构的有机电致发光器件,测试了其电致发光性能,研究结果表明此种方法有助于延长有机电致发光器件的寿命.
参考文献
| [1] | Tang C W;VanSlyke S A .[J].Applied Physics Letters,1987,51:913-915. |
| [2] | Choi J W;Kim J S;Oh S Y et al.[J].Thin Solid Films,2000,363(1-3):271-274. |
| [3] | Kawaharada M;Ooishi M;Saito T et al.[J].Synthetic Metals,1997,91(1-3):113-116. |
| [4] | Lim SF.;Chua SJ.;Wang W. .Degradation of organic light-emitting devices due to formation and growth of dark spots[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2001(2/3):154-159. |
| [5] | 黄大勇,牛萍娟,李晓云.有机电致发光器件封装技术的研究进展[J].微电子学,2010(06):875-879. |
| [6] | D'Andrade B W;Giebink N C;Weaver M S et al.[J].Nature Photonics,2007,1:33-36. |
| [7] | 卫芳芳,王华,徐阳,侯建新,周禾丰,许并社.8-羟基喹啉金属配合物的制备与提纯[J].人工晶体学报,2009(03):756-760,776. |
| [8] | Xu B S;Chen L Q;Liu X G et al.[J].Applied Physics Letters,2008,92(10):1033-1036. |
| [9] | Ozasa K;Nemoto S;Isoshima T et al.[J].Applied Physics Letters,2008,93:263304. |
| [10] | Xu W;Brauer J;Szulczewski G et al.[J].Applied Physics Letters,2009,94:233302. |
| [11] | Brinkmann M;Fite B;Pratontep S et al.[J].Chemistry of Materials,2004,16:4627-4633. |
| [12] | 覃操,王亭杰,金涌.液相沉积法制备TiO2颗粒表面包覆SiO2纳米膜[J].物理化学学报,2002(10):884-889. |
| [13] | Leung LM.;So SK.;Lee KM.;Choi WK.;Lo WY. .A high-efficiency blue emitter for small molecule-based organic light-emitting diode[J].Journal of the American Chemical Society,2000(23):5640-5641. |
| [14] | 刘世宏;王当憨;潘承璜.X射线光电子能谱分析[M].北京:科学出版社,1988 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%