在14.5 mm制式弹弹头部采用非金属Tc材料，并与制式弹进行对比，在相同装药量的情况下，试验研究了两种弹丸对陶瓷复合靶的侵彻能力。采用ANSYS-LS/DYNA进行模拟仿真，并与试验结果对比，模拟结果与试验结果基本吻合，Tc复合弹侵彻装甲钢板形成冲塞，并在装甲钢背面有鼓包，鼓包周围有明显的裂纹。结果表明，Tc复合弹对陶瓷/钢复合靶的侵彻能力优于制式弹。
New nonmetal Tc materials were used as 14.5 mm standard bullet head and the bullet was compared with standard bullet. Under the condition of the same charge,experimental study of two kinds of projectiles penetrating ceramic composite target was carried out. The LS?DYNA software was used to simulate,the comparison with the experiment results was made. The results show that the simulation results agree well with the test results,plugging damage is formed when the Tc composite bullet penetrates armor,and armor steel back has obvious bulging,obvious cracks are observed around bulging,penetration ability of Tc composite bullet is better than that of the standard bullet.
参考文献
| [1] | 黄燕玲,吴卫国,李晓彬,徐双喜,孔祥韶.爆炸破片侵彻钢/陶瓷/铝复合板的数值计算研究[J].中国舰船研究,2010(04):27-31. |
| [2] | 李平 .陶瓷材料的动态力学响应及其抗长杆弹侵彻机理[D].北京理工大学,2002. |
| [3] | 胡丽萍,钟涛,王智慧,侯圣英,郭领.不同厚度陶瓷与钢背板复合抗弹丸穿甲能力的实验研究[J].弹箭与制导学报,2010(03):63-65. |
| [4] | 周楠,王金相,董刚,杨瑞.功能梯度复合靶冲击毁伤研究进展[J].科学技术与工程,2011(12):2752-2761. |
| [5] | 罗韶华 .陶瓷复合装甲抗侵彻机理与性能的理论与实验研究[D].湖南大学,2009. |
| [6] | 蒋志刚,申志强,曾首义,谭清华.穿甲子弹侵彻陶瓷/钢复合靶板试验研究[J].弹道学报,2007(04):38-42. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%