采用电子背散射衍射(EBSD)技术研究在1075℃、初始应变速率1.5×10-3s-1条件下大晶粒Ni-48Al合金超塑变形过程中的组织演变.结果表明,变形前,大晶粒Ni-48Al合金以大角度晶界为主,小角度晶界比例极低.在超塑变形过程中,持续有取向差≤5°的小角度晶界产生.随变形量的增大,新形成的小角度晶界取向差增加,转变为取向差6°~15°小角度晶界,进而转变为取向差>15°的大角度晶界.小角度晶界的产生速率与小角度晶界转变为较大角度晶界的速率趋向一动态平衡.小角度晶界向较大角度晶界不断转变的结果使大角度晶界数量不断增加,最终导致晶粒显著细化.
参考文献
| [1] | Venables J A;Harland C J .[J].Philosophical Magazine,1973,27(05):1193. |
| [2] | Wright S I .[J].Journal D Computer Assisted Microscopy,1993,5(03):207. |
| [3] | Cao W Q;Godfrey A;Lhi W et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2003,360:420. |
| [4] | Jiang J;Godfrey A;Liu W;Liu Q .Microtexture evolution via deformation twinning and slip during compression of magnesium alloy AZ31[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(0):576-579. |
| [5] | Wang, Y;Shao, WZ;Zhen, L;Zhang, XM .Microstructure evolution during dynamic recrystallization of hot deformed superalloy 718[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1/2):321-332. |
| [6] | Sonderegger, B;Mitsche, S;Cerjak, H.Microstructural analysis on a creep resistant martensitic 9-12% Cr steel using the EBSD method[J].Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008:466-470. |
| [7] | Ferry M;Burhan N .[J].Scripta Materialia,2007,56:525. |
| [8] | Sanchez-Hanton J J;Thomson R C .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2007,460-461:261. |
| [9] | Jia N;Lin R;Chai G C .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2008,491:425. |
| [10] | Chen Y J;Wang Q D;Roven H J et al.[J].Journal of Alloys and Compounds,2008,462:192. |
| [11] | Dehghan-Manshadi A;Barnett MR;Hodgson PD .Recrystallization in AISI 304 austenitic stainless steel during and after hot deformation[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):664-672. |
| [12] | Xue Q;Bingert JF;Henrie BL;Gray GT .EBSD characterization of dynamic shear band regions in pre-shocked and as-received 304 stainless steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):279-289. |
| [13] | Evans W J;Jones J P;Whittaker M T .[J].International Journal of Fatigue,2005,27:1244. |
| [14] | Hu Jing;Lin Donliang .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2004,371:113. |
| [15] | Hu Jing;Lin Donliang .[J].Materials Letters,2004,58:1297. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%