Porous calcium phosphate ceramics were produced by compression molding using a special mold followed by sintering. The porous calcium phosphate ceramics have three-dimensional and penetrated open pores380-400μm in diameter spaced at intervals of 200μm. The layers of the linear penetration pores alternately lay perpendicular to pore direction. The porosity was 59%-65% . The Ca/P molar ratios of the porous calcium phosphate ceramics range from 1.5 to 1.85. A binder containing methyl cellulose was most effective for preparing the powder compact among vinyl acetate, polyvinyl alcohol, starch, stearic acid, methyl cellulose and their mixtures. Stainless steel, polystyrene, nylon and bamboo were used as the long columnar male dies for the penetrated open pores. When polystyrene, nylon and bamboo were used as the long columnar male dies, the dies were burned out during the sintering process. Using stainless steel as the male dies with the removal of the dies before heat treatment resulted in a higher level of densification of the calcium phosphate ceramic.
参考文献
| [1] | Chang BS;Lee CK;Hong KS;Youn HJ;Ryu HS;Chung SS;Park KW .Osteoconduction at porous hydroxyapatite with various pore configurations.[J].Biomaterials,2000(12):1291-1298. |
| [2] | Peelen J P et al.Sintered Hydroxylapatite as a Bioceramic[J].Philips Technological Review,1978,37:234-236. |
| [3] | Tamai N;Myoui A;Tomita T;Nakase T Tanaka J Ochi T Yoshikawa H .Novel Hydroxyapatite Geramics with an Interconnective Porous Structure Exhibit Superior Osteoconduction in vivo[J].Journal of Biomedical Materials Research Part A,2002,59:110-117. |
| [4] | Tsuzuki M;Kondo K .Methods to Prepare Calcium Phosphate Porous Ceramics[P].JP 3096930,2000. |
| [5] | Kurosawa H;Aoki H;Akao M .Tissue Reactions to Calcined Bone Graft[J].Biomaterials,1986,7:132-136. |
| [6] | Roy D M;Linnehan S K .Hydroxyapatite Formed from Coral Skeletal Garbonate by Hydrothermal Exchange[J].Nature,1974,247:220-222. |
| [7] | Chu T-M G;Halloran J W;Hollister S J;Feinberg S E .Hydroxyapatite Implants with Designed Internal Architecture[J].Journal of Materials Science:Materials in Medicine,2001,12:471-478. |
| [8] | Erik Adolfsson .Macro Porous Hydroxyapatite with Designed Pores[J].Key engineering materials,2004(254/256):1025-1028. |
| [9] | Hollister S J;Lin C Y;Saito E;Lin G Y, Schek R D, Taboas J M, Williams J M, Partee B, Flanagan C L, Diggs A, Wilke E N, Van Lenthe G H, Müller R, Wirtz T, Das S, Feinberg S E, Krebsbach P H .Engineering Craniofacial Scaffolds[J].Orthodontics and Craniofacial Research,2005,8:162-173. |
| [10] | Chu TM;Orton DG;Hollister SJ;Feinberg SE;Halloran JW .Mechanical and in vivo performance of hydroxyapatite implants with controlled architectures.[J].Biomaterials,2002(5):1283-1293. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%