本文采用水热法,在430℃,35%填充度,反应24h合成了ZnO晶体.当矿化剂浓度较低时,如1mol·L-1NaOH,只合成了ZnO微晶.提高矿化剂浓度可以合成出个体较大晶体,如采用5 mol·L-1NaOH作矿化剂时,合成晶体的长度达到500μm.以3mol·L-1 KOH作矿化剂时,合成晶体的长度为1500μm.以3 mol·L-1NaOH和1mol·L-1KBr作矿化剂时合成晶体的长度为700μm,直径200 μm,显露完整的晶面,显示晶体有较高的质量.除了大的晶体以外,合成产物中有大量的微晶和纳米晶簇.
参考文献
| [1] | Bagnall DM;Chen YF;Zhu Z;Yao T;Koyama S;Shen MY;Goto T .Optically pumped lasing of ZnO at room temperature[J].Applied physics letters,1997(17):2230-2232. |
| [2] | Tang ZK.;Yu P.;Kawasaki M.;Ohtomo A.;Koinuma H.;Segawa Y.;Wong GKL. .Room-temperature ultraviolet laser emission from self-assembled ZnO microcrystallite thin films[J].Applied physics letters,1998(25):3270-3272. |
| [3] | Bagnall DM.;Zhu Z.;Yao T.;Shen MY.;Goto T.;Chen YF. .High temperature excitonic stimulated emission from ZnO epitaxial layers[J].Applied physics letters,1998(8):1038-1040. |
| [4] | 郭常新,傅竹西,施朝淑.阴极射线激发下ZnO薄膜室温紫外发光的超线性增长规律[J].发光学报,1998(03):239-241. |
| [5] | 吕树臣,宋国利,肖芝燕,张家骅,黄世华.纳米氧化锌粉体的制备及发光性质的研究[J].发光学报,2002(03):306-310. |
| [6] | Garces N Y;Wang L;Bai L et al.[J].Applied Physics Letters,2002,18(04):622-624. |
| [7] | 井立强,孙晓君,徐自力,蔡伟民,杜尧国.ZnO超微粒子光催化氧化SO2的研究[J].催化学报,2002(01):37-40. |
| [8] | 井立强,郑莹光,徐自力,董凤霞,孙晓君,蔡伟民,徐英凯.ZnO超微粒子的EPR特性和光催化性能[J].高等学校化学学报,2001(11):1885-1888. |
| [9] | 井立强,徐自力,杜尧国,孙晓君,王玲,周秀清,单洪岩,蔡伟民.ZnO超微粒子光催化氧化降解n-C7H16的研究[J].高等学校化学学报,2002(05):871-875. |
| [10] | 杨青林,郭林,吴中华,江雷,徐文国,李前树.室温下纳米氧化锌新相的合成及表征[J].高等学校化学学报,2003(01):82-85. |
| [11] | 王振旅,马红超,朱万春,于剑锋,王国甲.在纳米Cu-ZnO上仲丁醇的催化脱氢[J].高等学校化学学报,2002(11):2163-2165. |
| [12] | 丁士文,张绍岩,刘淑娟,丁宇,康全影,刘燕朝.直接沉淀法制备纳米ZnO及其光催化性能[J].无机化学学报,2002(10):1015-1019. |
| [13] | 李旦振,陈亦琳,林熙,王绪绪,付贤智.纳米ZnO的制备及发光特性研究[J].无机化学学报,2002(12):1229-1232. |
| [14] | Hou T. Ng;Jun Li;Michael K. Smith;Pho Nguyen;Alan Cassell;Jie Han;M. Meyyappan .Growth of Epitaxial Nanowires at the Junctions of Nanowalls[J].Science,2003(5623):1249-0. |
| [15] | Huang Michael H;Mao Samuel;Feick Henning et al.[J].Science,2001,292(08):1897-1899. |
| [16] | Yan Haoquan;He Rongrui;Juhnson Justin et al.[J].Journal of the American Chemical Society,2003,125(16):4728-4729. |
| [17] | 华素坤.热液条件下ZnO晶体的形成机理[J].人工晶体学报,1994(03):177. |
| [18] | 王步国.ZnO晶体的极性生长习性与双晶的形成机理[J].人工晶体学报,1997(02):102. |
| [19] | 张军,孙聆东,廖春生,严纯华.氧化锌微晶的制备和形貌控制[J].无机化学学报,2002(01):72-74. |
| [20] | 李汶军;施尔畏;田明原 等.[J].中国科学E辑,1998,28(03):212-219. |
| [21] | Liu B;Zeng H C .[J].Journal of the American Chemical Society,2003,125(15):4430-4431. |
| [22] | Guo L;Ji L;Xu H et al.[J].Journal of the American Chemical Society,2002,124(50):14864-14865. |
| [23] | Urbieta A.;Piqueras J.;Hardalov C.;Sekiguchi T.;Fernandez P. .Cathodoluminescence microscopy of hydrothermal and flux grown ZnO single crystals[J].Journal of Physics, D. Applied Physics: A Europhysics Journal,2001(19):2945-2949. |
| [24] | Sekiguchi T.;Obara K.;Shishido T.;Sakagami N.;Miyashita S. .Hydrothermal growth of ZnO single crystals and their optical characterization[J].Journal of Crystal Growth,2000(0):72-76. |
| [25] | Eriko Ohshima;Hiraku Ogino;Ikuo Niikura;Katsumi Maeda;Mitsuru Sato;Masumi Ito;Tsuguo Fukuda .Growth of the 2-in-size bulk ZnO single crystals by the hydrothermal method[J].Journal of Crystal Growth,2004(1/2):166-170. |
| [26] | Florescu D I;Mourokh L G;Pollak F H et al.[J].Journal of Applied Physics,2002,91(02):890-892. |
| [27] | 韦志仁,董国义,王立明,李志强,张华伟.矿化剂浓度和温度对水热法合成氧化锌晶体形态的影响[J].发光学报,2003(04):353-357. |
| [28] | 董国义,韦志仁,林岩,王立明,李志强,张华伟.水热法合成氧化锌晶体[J].人工晶体学报,2003(02):130-133. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%