采用激光引燃自蔓延技术合成铝-钛-硼中间合金,利用此中间合金可对ZL108铝合金组织进行细化,研究了激光辐照参数对中间合金和铝合金显微组织的影响.结果表明:通过对激光器工作参数的调整,可制备出具有TiAl3和TiB2颗粒含量适中、弥散分布的中间合金;在本试验条件下,激光功率1 200 W、照射1.0 s时,生成粒径约为1μm、弥散分布的TiB2,长度约10μm、均匀分布的长条状TiAl3,此时中间合金的细化效果最佳,铝晶粒平均尺寸为55 μm.
参考文献
| [1] | Limmaneevichitr C.;Eidhed W. .Fading mechanism of grain refinement of aluminum-silicon alloy with Al-Ti-B grain refiners[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):197-206. |
| [2] | K. Venkateswarlu;M. Chakraborty;B.S. Murty .Influence of thermo-mechanical processing of Al-5Ti-1B master alloy on its grain refining efficiency[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):75-83. |
| [3] | 张虎,高文理,张二林,曾松岩.Ti-54Al-xB合金中TiB2的形貌演变及生长机理[J].金属学报,2002(07):699-702. |
| [4] | Peijie Li;E.G. Kandalova;V.I. Nikitin;A.R. Luts;A.G. Makarenko;Yanfei Zhang .Effect of fluxes on structure formation of SHS Al―Ti―B grain refiner[J].Materials Letters,2003(22/23):3694-3698. |
| [5] | 张作贵,刘相法,边秀房,马家骥.AlTiB中间合金中的化合物形态[J].中国有色金属学报,1999(04):736-739. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%