研究了Waspaloy高温合金在扩大锭型后,铸锭中元素偏析程度和均匀化处理过程中元素偏析规律并建立理论模型.采用光学显微镜、扫描电镜、能谱仪分析了该合金铸态和均匀化态的显微组织和元素的偏析规律,以此为基础分析并建立了偏析指数与材料工艺参数的关系,为扩大锭型后均匀化制度的合理制订提供理论依据.同时认为φ508 mm铸锭的均匀化应分为2个阶段进行,第l阶段为1120℃的低熔点组织溶解,第2阶段为1180℃左右进行Ti,Cr元素的扩散,改善偏析.结果表明:合金在1180℃退火20 h较合理.
参考文献
| [1] | Semiatin S et al.[J].Scripta Materialia,2004,51:491. |
| [2] | Karunaratne.Superalloys 2000[M].Warrendale:TMS,2000:263. |
| [3] | Kadalbal R et al.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1982,13A:1153. |
| [4] | Penkalla HJ.;Wosik J.;Czyrska-Filemonowicz A. .Quantitative microstructural characterisation of Ni-base superalloys[J].Materials Chemistry and Physics,2003(2/3):417-423. |
| [5] | Keh Minn Chang;Liu Xingbo .[J].Materials Science and Engineering A,2001,308(01) |
| [6] | Jaroslaw Wosik;Beata Dubiel;Adam Kruk .Stereological estimation of microstructural parameters of nickel-based superalloy Waspaloy using TEM methods[J].Materials Characterization,2001(2/3):119-123. |
| [7] | 仲增墉;庄景云 .[J].钢铁研究,2003,15(07):1. |
| [8] | 龙正东,邓群,林平,马培立,庄景云,仲增塘.热处理对GH742合金组织和力学性能的影响[J].材料工程,1999(03):41-44. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%