为探究连续热镀锌气刀射流拭锌过程中发生的带钢边部压力衰减问题，设计了气流冲击平板实验，对带钢表面气流流向及压力进行测定。基于测量的参数，对该气刀射流喷吹过程进行数值模拟，并结合所推导的镀层厚度计算模型，对为减少带钢边部压力衰减所增设的边部挡板进行了厚度优化。研究结果表明：气刀喷吹时带钢边部气流发生横向偏转，使得带钢边部压力较中心处低，气压衰减率随气刀与带钢的间隔距离增加而增加，增设边部挡板能有效阻碍带钢边部压力衰减和降低边部过镀锌缺陷发生，且挡板厚度为2 mm时的作用效果最佳。
To explore the strip edge pressure decreases as gas?jet wiping in hot?dip galvanizing process, a gas impact plate experiment was carried out, and the process of gas jet wiping was also simulated using the measured results. The added edge baffle near the edge of strip which is used to prevent the wall pressure decreases in strip edge was optimized with the help of the analytic model of film thickness. The results show that the airflow of strip edge occurs lateral deflection and the wall pressure in the strip edge is lower than those in center, in addition, the edge air pressure attenuation increases with the rising distance between the air knife and the strip. The edge pressure decreases and the edge over coating problem can be reduced effectively by adding edge baffle, and the best result happens when the thickness of baffle is 2 mm.
参考文献
| [1] | 张启富;刘邦津;黄健中.现代钢带连续热镀锌[M].北京:冶金工业出版社,2007:396-399. |
| [2] | ZHANG Yan,CUI Qi-peng,SHAO Fu-qun,WANG Jun-sheng,ZHAO Hong-yang.Influence of Air-Knife Wiping on Coating Thickness in Hot-Dip Galvanizing[J].钢铁研究学报：英文版,2012(06):70-78. |
| [3] | 张红,杜翠薇,李晓刚.热镀锌板在3种典型泥浆中的电化学阻抗谱特征[J].材料科学与工艺,2010(02):154-158. |
| [4] | 余金山,刘俊亮,张津徐,吴建生.合金化热镀锌镀层组织Г相的结构分析[J].材料科学与工艺,2008(01):99-102. |
| [5] | Yoshiaki TAKEISHI;Hisakazu MORINO .Mechanism and Prevention of Edge Over Coating in Continuous Hot-Dip Galvanizing[J].ISIJ International,2000(11):1127-1133. |
| [6] | 岑耀东.热镀锌薄钢板边部过镀锌的产生机理及预防[J].金属热处理,2011(06):134-136. |
| [7] | 刘金华.边部增厚缺陷的产生机理及其控制措施[J].梅山科技,2012(06):56-58. |
| [8] | Sang Joon KIM;Joong Won CHO;Ki Jang AHN;Myung Kyoon CHUNG .Numerical Analysis of Edge Over-coating in Continuous Hot-dip Galvanizing[J].ISIJ International,2003(10):1495-1501. |
| [9] | Ki Jang AHN;Myung Kyoon CHUNG .A noble gas wiping system to prevent the edge overcoating in continuous hot-dip galvanizing[J].ISIJ International,2006(4):573-578. |
| [10] | Tae-Seok CHO,Young-Doo KWON,Soon-Bum KWON.A Study of the Influence of Air-knife Tilting on Coating Thickness in Hot-dip Galvanizing[J].热科学学报（英文版）,2009(03):262-267. |
| [11] | 杨钢,高隆隆,李宝仁.新型高压电-气伺服阀阀口气体射流数值研究[J].机械工程学报,2013(02):165-173. |
| [12] | Lacanette D;Gosset A;Vincent S;Buchlin JM;Arquis E .Macroscopic analysis of gas-jet wiping: Numerical simulation and experimental approach[J].Physics of fluids,2006(4):42103-1-42103-15-0. |
| [13] | Hongyun SO;Hyun Gi YOON;Myung Kyoon CHUNG .CFD Analysis of Sag Line Formation on the Zinc-coated Steel Strip after the Gas-jet Wiping in the Continuous Hot-dip Galvanizing Process[J].ISIJ International,2011(1):115-123. |
| [14] | NAPHADE P;MUKHOPADHYAY A;CHAKRABAR-TI S .Mathematical modeling of jet finishing process for hot-dip zinc coatings on steel strip[J].ISIJ Interna-tional,2005,45(02):209-210. |
| [15] | THORNTON J A .An analytical description of the jet finishing process for hot-dip metallic coating on strip[J].Metallurgical Transactions B,1976,7B:607-618. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%