通过LCR宽频数字电桥直接测量LC4铝合金阳极氧化膜封孔前后的各种电参数变化,获得封孔信息,评价封孔质量;同时与测得的极化曲线、电化学交流阻抗谱进行对比,并结合FESEM和EDS对结果进行分析,结果表明,使用LCR宽频数字电桥评价铝合金阳极氧化膜的封孔质量,数据规律性强,操作简单易行.
参考文献
| [1] | 李长虹,李荻.涂漆铝合金体系的腐蚀电化学研究方法[J].航空工程与维修,2001(5):21-23. |
| [2] | Patermarakis G;Papadreadis N .Effect of the structure of porous anodic Al2O3 films on the mechanism of their hydrothermal treatment[J].Electrochimica Acta,1993,38(10):1413-1420. |
| [3] | Thompson GE. .POROUS ANODIC ALUMINA - FABRICATION, CHARACTERIZATION AND APPLICATIONS[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1997(1/2):192-201. |
| [4] | 王海潮,彭乔,王啸宇,李清启.电化学法研究铝阳极氧化膜的抗腐蚀性[J].腐蚀与防护,2006(08):391-393. |
| [5] | Habazaki H.;Skeldon P.;Thompson GE.;Wood GC.;Shimizu K. .FORMATION OF AMORPHOUS ANODIC OXIDE FILMS OF CONTROLLED COMPOSITION ON ALUMINIUM ALLOYS[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1997(1/2):131-137. |
| [6] | Suay J J;Gimenez E .Characterization of anodized and sealed aluminium by EIS[J].Corrosion Science,2003,45:611-624. |
| [7] | 田连朋,左禹,赵景茂,熊金平,赵旭辉.铝合金阳极氧化膜醋酸镍封闭方法耐蚀性研究[J].腐蚀与防护,2006(02):58-62. |
| [8] | 赵鹏辉,左禹.硬脂酸封闭工艺参数对铝阳极氧化膜耐蚀性的影响[J].材料保护,2002(05):30-31,39. |
| [9] | 程红霞,罗静,尹茂生,廖广其.铝合金铬酸阳极氧化膜的低铬封孔工艺研究[J].材料保护,2004(07):32-32,51. |
| [10] | 田连朋,左禹,赵景茂,熊金平,张晓丰,赵旭辉.LD7铝合金阳极氧化膜的不同封闭方法耐蚀性评价[J].中国腐蚀与防护学报,2005(06):327-331. |
| [11] | 旷亚非,王玲,曾凌三.铝阳极氧化多孔膜的离子导电性与封孔性能[J].电镀与精饰,1999(03):20-23. |
| [12] | 李宜;朱祖芳;江志裕 等.铝阳极氧化膜冷封孔机理研究:Ⅰ.冷封孔氧化膜的组成结构[J].中国腐蚀与防护学报,1992,12(04):315-320. |
| [13] | 朱祖芳.铝合金阳极氧化与表面处理技术[M].北京:化学工业出版社,2004:229. |
| [14] | Hitzig J;Juttner K;Lorenz W J et al.AC impedance measurements on porous aluminium oxide films[J].Corrosion Science,1984,24(11-12):945-952. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%