采用摩尔分数1%Ni及负载少量Mo的Ni/MO/MgO催化剂裂解甲烷合成薄壁碳纳米管.通过SEM、TEM、XRD和Raman光谱表征方法研究了碳纳米管直径和催化剂中Ni/Mo比例关系.实验发现:通过控制Ni/Mo比例可以调变催化剂颗粒大小以及活性相.TEM及XRD表征发现,随着Ni/Mo比例的降低,金属Mo相逐渐从NiMo合金相中析出.NiMo合金相对应的活性组分颗粒很小,容易催化裂解甲烷形成薄壁碳纳米管;而后析出的Mo相则主要形成了大管径厚壁的碳纳米管.当Ni/Mo比例为6时可以高选择性地获得窄分布,内径为1.3nm,外径为3.0nm的溥壁碳纳米管.Raman光谱进一步验证了碳纳米管含有较少的缺陷.薄壁碳纳米管形成的关键因素主要体现为碳在其表而的快速扩散以及小颗粒的碳纳米管催化剂活性相控制.
Thin-walled carbon nanotubes (CNTs) were prepared from methane decomposition using Ni/Mo/MgO as catalysts loaded with 1% mole fraction of Ni and smaller proportion of Mo.The relationship between CNT diameter and Ni/Mo ratio was studied by SEM,TEM,XRD and Raman spectroscopy.The particle size and the active phase of the catalyst could be modulated by the Ni/Mo ratio.With decreasing Ni/Mo ratio,a NiMo alloy was first formed,and then an isolated Mo phase was formed on the catalyst,as characterized by TEM and XRD.The NiMo alloy,with very small size,was responsible for the growth of thin-walled CNTs,whereas,the Mo phase was related to the formation of largediameter thick-walled CNTs.The thin-walled CNTs with outer diameter of 3.0 nm and inner diameter of 1.3 nm could be obtained with high selectivity,a narrow diameter distribution,and high purity by controlling the Ni/Mo ratio at 6.Raman spectra confirmed the formation of thin-walled CNTs with few defects.The formation of thin-walled CNTs was mainly attributed to a rapid surface diffusion and precipitation of carbon on the small metal alloy crystallites.
参考文献
| [1] | Baughman R H;Zakhidov A A;de Heer W A .Carbon nanotubes-the route toward applications[J].Science,2002,297(5582):787-792. |
| [2] | Dalton AB;Collins S;Munoz E;Razal JM;Ebron VH;Ferraris JP .Super-tough carbon-nanotube fibres - These extraordinary composite fibres can be woven into electronic textiles.[J].Nature,2003(6941):703-0. |
| [3] | Jonathan N. Coleman;Umar Khan;Werner J. Blau .Small but strong: A review of the mechanical properties of carbon nanotube-polymer composites[J].Carbon: An International Journal Sponsored by the American Carbon Society,2006(9):1624-1652. |
| [4] | 吴锋,徐斌.碳纳米管在超级电容器中的应用研究进展[J].新型炭材料,2006(02):176-184. |
| [5] | 魏飞,张强,骞伟中,徐光辉,项荣,温倩,王垚,罗国华.碳纳米管阵列研究进展[J].新型炭材料,2007(03):271-282. |
| [6] | Branimir Lukic;Jin Won Seo;Revathi R.Bacsa;Sandrine Delpeux;Francois Beguin .Catalytically Grown Carbon Nanotubes of Small Diameter Have a High Young's Modulus[J].Nano letters,2005(10):2074-2077. |
| [7] | de Jonge, N;Allioux, M;Doytcheva, M;Kaiser, M;Teo, KBK;Lacerda, RG;Milne, WI .Characterization of the field emission properties of individual thin carbon nanotubes[J].Applied Physics Letters,2004(9):1607-1609. |
| [8] | Willems I. .Control of the outer diameter of thin carbon nanotubes synthesized by catalytic decomposition of hydrocarbons[J].Chemical Physics Letters,2000(1/2):71-76. |
| [9] | Ling-Ping Zhou;Keishin Ohta;Keiji Kuroda;Ni Lei;Kiyoto Matsuishi;Lizhen Gao;Taketoshi Matsumoto;Junji Nakamura .Catalytic Functions of Mo/Ni/MgO in the Synthesis of Thin Carbon Nanotubes[J].The journal of physical chemistry, B. Condensed matter, materials, surfaces, interfaces & biophysical,2005(10):4439-4447. |
| [10] | Weizhong Qian;Tang Liu;Fei Wei .Carbon nanotubes containing iron and molybdenum particles as a catalyst for methane decomposition[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(4):846-848. |
| [11] | Y.Li;X.B.Zhang;X.Y.Tao;J.H.Luo;Z.Q.Luo;T.Li;F.Liu .Mass production of high-quality multi-walled carbon nanotube bundles on a Ni/Mo/MgO catalyst[J].Carbon: An International Journal Sponsored by the American Carbon Society,2005(2):295-301. |
| [12] | Shimizu Y.;Sasaki T.;Kodaira T.;Kawaguchi K.;Terashima K.;Koshizaki N. .Fabrication of carbon nanotube assemblies on Ni-Mo substrates mimics law of natural forest growth[J].Chemical Physics Letters,2003(5-6):774-780. |
| [13] | Herrera JE.;Borgna A.;Alvarez WE.;Resasco DE.;Balzano L. .Relationship between the structure/composition of Co-Mo catalysts and their ability to produce single-walled carbon nanotubes by CO disproportionation[J].Journal of Catalysis,2001(1):129-145. |
| [14] | Pierre Coquay;Emmanuel Flahaut;Eddy De Grave;Alain Peigney;Robert E.Vandenberghe .1.Fe/Co Alloys for the Catalytic Chemical Vapor Deposition Synthesis of Single-and Double-Walled Carbon Nanotubes(CNTs).2.The CNT-Fe/Co-MgAl_2O_4 System[J].The journal of physical chemistry, B. Condensed matter, materials, surfaces, interfaces & biophysical,2005(38):17825-17830. |
| [15] | 王茂章,李峰,杨全红,成会明.由不同碳源合成及制备纳米碳管的进展[J].新型炭材料,2003(04):250-264. |
| [16] | 李颖,李轩科,刘朗.不同原料气催化热解法制备碳纳米管的研究[J].新型炭材料,2004(04):298-302. |
| [17] | 刘云芳,沈曾民,马宝海,于建民.碳源对碳纳米管形态的影响[J].新型炭材料,2003(04):295-299. |
| [18] | 卢怡,朱珍平,刘振宇.催化剂对爆炸法合成碳纳米管的影响[J].新型炭材料,2004(01):1-6. |
| [19] | 郑瑞廷,程国安,赵勇,刘华平,梁昌林.乙炔催化裂解制备碳纳米带及其结构表征[J].新型炭材料,2005(04):355-359. |
| [20] | Weizhong Qian;Hao Yu;Fei Wei;Qunfeng Zhang;Zhanwen Wang .Synthesis of carbon nanotubes from liquefield petroleum gas containing sulfur[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(15):2968-2970. |
| [21] | Hee Cheul Choi;Woong Kim;Dunwei Wang;Hongjie Dai .Delivery of Catalytic Metal Species onto Surfaces with Dendrimer Carriers for the Synthesis of Carbon Nanotubes with Narrow Diameter Distribution[J].The journal of physical chemistry, B. Condensed matter, materials, surfaces, interfaces & biophysical,2002(48):12361-12365. |
| [22] | Y. Li;X.B. Zhang;X.Y. Tao .Single phase MgMoO_4 as catalyst for the synthesis of bundled multi-wall carbon nanotubes by CVD[J].Carbon: An International Journal Sponsored by the American Carbon Society,2005(6):1325-1328. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%