用于太阳电池窗口层的材料必须具有好的耐蚀性.利用射频磁控溅射的方法分别在300℃、350℃、400℃、450℃的沉积温度下制备透明导电Sc掺杂ZnO薄膜(SZO).用X射线衍射仪对样品的结构进行表征.结果表明,所有SZO薄膜均为六角纤锌矿结构,在(002)衍射峰位上相对于纯ZnO粉末有微小的偏移.用动电位扫描极化曲线和交流阻抗谱表征SZO薄膜的耐腐蚀性能,研究结果表明随沉积温度的升高,SZO薄膜的耐腐蚀性增强.在可见光范围内SZO薄膜透过率达85％以上,经3.5％的NaCl溶液腐蚀24h后薄膜透过率仍在80％以上.
参考文献
| [1] | Roy C.;Byrne S.;McGlynn E.;Mosnier JP.;de Posada E.;O'Mahony D. Lunney JG.;Henry MO.;Ryan B.;Cafolla AA. .Correlation of Raman and X-ray diffraction measurements of annealed pulsed laser deposited ZnO thin films[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2003(2):273-276. |
| [2] | Chen ZQ;Kawasuso A;Xu Y;Naramoto H;Yuan XL;Sekiguchi T;Suzuki R;Ohdaira T .Production and recovery of defects in phosphorus-implanted ZnO[J].Journal of Applied Physics,2005(1):3528-1-3528-6-0. |
| [3] | Jin Z C;Hamberg I;Granqvist C G et al.Optical Properties of Sputter-deposited ZnO:Al Thin Films[J].Journal of Applied Physics,1988,64(10):5117-5131. |
| [4] | Major S;Kumar S;Bhatnagar M et al.Effect of Hydrogen Plasma Treatment on Transparent Conducting Oxides[J].Applied Physics Letters,1986,49(07):394-396. |
| [5] | Calnan S;Hupkes J;Rech B;Siekmann H;Tiwari A .High deposition rate aluminium-doped zinc oxide films with highly efficient light trapping for silicon thin film solar cells[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2008(6):1242-1248. |
| [6] | Do-Hyun Kim;Hoonha Jeon;Geumchae Kim;Suejeong Hwangboe;Ved Prakash Verma;Wonbong Choi;Minhyon Jeon .Comparison of the optical properties of undoped and Ga-doped ZnO thin films deposited using RF magnetron sputtering at room temperature[J].Optics Communications: A Journal Devoted to the Rapid Publication of Short Contributions in the Field of Optics and Interaction of Light with Matter,2008(8):2120-2125. |
| [7] | Tadatsugu Minami;Takashi Yamamoto;Toshihiro Miyata .Highly transparent and conductive rare earth-doped ZnO thin films prepared by magnetron sputtering[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2000(1/2):63-68. |
| [8] | Jing-Chie Lin;Kun-Cheng Peng;Hsueh-Lung Liao;Sheng-Long Lee .Transparent conducting Sc-codoped AZO film prepared from ZnO:Al-Sc by RF-DC sputtering[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2008(16):5349-5354. |
| [9] | Lin, JC;Peng, KC;Tseng, CA;Lee, SL .Deposition of Al-doped and Al, Sc-co-doped zinc oxide films by RF- and DC-sputtering of the ZnO and Al-xSc (x=0, 0.4, 0.8 and 1.7 wt.%) targets[J].Surface & Coatings Technology,2008(22/23):5480-5483. |
| [10] | Jing-Chie Lin;Kun-Cheng Peng;Iran-Gying Peng;Sheng-Long Lee .Corrosion behavior of Al, Sc-co-doped ZnO thin films in 3.5% NaCl solution[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2009(17):4777-4781. |
| [11] | Kajikawa Y .Texture development of non-epitaxial polycrystalline ZnO films[J].Journal of Crystal Growth,2006(1):387-394. |
| [12] | Matsuoka M;Ono K .Photochromism and Anomalous Crystallite Orientation of ZnO Films Prepared by a Spuuering-type Electron Cyclotron Resonance Microwave Plasma[J].Applied Physics Letters,1988,53(15):1393-1395. |
| [13] | Kim KS.;Kim HW.;Kim NH. .Structural characterization of ZnO films grown on SiO2 by the RF magnetron sputtering[J].Physica, B. Condensed Matter,2003(3/4):343-346. |
| [14] | Cullity B D.Elements of X-ray Diffractions[M].London:Addition-Wesley,1959:99. |
| [15] | Fang GJ.;Li DJ.;Yao BL. .Effect of vacuum annealing on the properties of transparent conductive AZO thin films prepared by DC magnetron sputtering[J].Physica Status Solidi, A. Applied Research,2002(1):139-152. |
| [16] | Chen, HX;Ding, JJ;Zhao, XG;Ma, SY .Microstructure and optical properties of ZnO:Al films prepared by radio frequency reactive magnetron sputtering[J].Physica, B. Condensed Matter,2010(5):1339-1344. |
| [17] | 徐飙,杜晓建,王龙妹,王福,冯海波.稀土对430铁素体不锈钢耐蚀性的影响[J].物理测试,2008(06):1-4. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%