基金项目: Open Research Fund of Key Laboratory of High Performance Complex Manufacturing,Central South University (Kfkt2013-04) Natural Science Foundation of Ningbo City (2013A610043,2013A610045) National Key Basic Research Development Program of China ("973" Program) (2014CB046502) Zhejiang Provincial Education Department Foundation (Y201224321) the Outstanding Youth Foundation of Zhejiang Province and K.C.Wong Magna Fund in Ningbo University (R1110646)

关键词：多楔楔横轧 , 大型厚壁空心长轴 , 椭圆度

Multi-wedge Cross Wedge Rolling Process of 42CrMo4 Large and Long Hollow Shaft

Keywords： multi-wedge cross wedge roiling , large and long thick-walled hollow shaft , ellipticity

大型厚壁空心长轴类零件是工业装备中的关键零部件,本研究采用多楔楔横轧成形该类零件.首先,推导多楔楔横轧长轴空心件的侧楔偏转角公式,为多楔楔横轧模具的设计奠定了基础.然后,研究展宽角对单楔楔横轧厚壁空心件的影响规律,发现相对于轧制小直径空心轴,展宽角的选择范围可以扩大,内孔椭圆度也能得到控制.同时发现模具的顶面脱空也能控制内孔椭圆度.最后,建立双楔楔横轧轧制大型厚壁空心长轴类零件的有限元模型,模拟了成形过程,监测对称面的内孔椭圆度,有限元计算的内孔椭圆度为4.98％,轧制实验值为5.56％.结果表明:双楔楔横轧大型厚壁空心长轴类零件是可行的.