采用普通模锻试验方法，研究了TC18高强度β锻造钛合金工艺参数与显微组织和力学性能之间的定量关系。结果表明：可以用一个新参数手β锻造综合参数）来表征以上加热温度与相变点温差T和单相区保温时间t对合金力学性能的综合影响；当取=T＋0．1t时，合金的断面收缩率中、冲击韧度aKU上升而线性下降；断裂韧度KE、疲劳极限D与之间具有峰值关系；芎与合金8晶粒平均直径D线性相关。
The TC18 titanium alloy was deformed by conventional die forging, lne relatlonsmp among p forging parameters, microstructure and mechanical properties of high strength titanium was been studied. The results show that the heating temperature above T(T) and holding time in zone(t) could be simplified as a new parameter forging integrate parameter) . While the value of d? (reduction of area) and impact toughness aKu descended linearly with the increase of fracture toughness Kc and fatigue limit aDhad a peak relations with and average grain diameter D had a linear correlation.
参考文献
| [1] | 曹春晓.选材判据的变化与高损伤容限钛合金的发展[J].金属学报,2002(z1):4-11. |
| [2] | 房卫萍,陈沦,史耀武,虞文军,毛智勇,唐振云.损伤容限钛合金的研究进展及应用现状[J].材料工程,2010(09):95-98. |
| [3] | 朱知寿,王庆如,郑永灵,王新南,周宇.损伤容限型钛合金新型β锻造工艺[J].中国有色金属学报,2004(z2):13-16. |
| [4] | 沙爱学,李兴无,王庆如,鲍如强.热变形温度对TC18钛合金显微组织和力学性能的影响[J].中国有色金属学报,2005(08):1167-1172. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%