Duplex stainless steels (DSS) with ferritic-austenitic microstructures offer good combination of resistance to pitting corrosion and high strength that are not concomitantly attainable using conventional single phase austenitic or ferritic stainless steels. The DSS used in this investigation was 2205 alloy having a stable mi-crostructure consisting of about 45% ferrite and 55% austenite at ambient temperature. In order to investigate aging behavior of this steel and the influences on mechanical properties, different aging treatments were conducted at temperatures of 350-950℃ for various aging time of 15, 30, 60 and 180 min. The aged specimens were subjected to impact testing and hardness measurements. Finally, the changes in microstructure due to aging were studied by optical and scanning electron microscopy. The results showed that aging at temperatures lower than 550℃ for different time had negligible effects on mechanical properties. Besides, no considerable changes in term of precipitation of harmful intermetallic particles were observed in microstructure below this temperature. However, a critical temperature range, 550-650 ℃, was introduced here. Aging in this range led to a significant decrease in toughness and notable increase in hardness. The formation of intermetallic phases such as σ was recognized as the major reason for the observed changes.
参考文献
[1] | J.Charles.[A].Beaune,Les editions de Physique,1991:3-48. |
[2] | H.D.Solomon;T.M.Devaine.Duplex Stainless Steels[M].ASM,Metals Park,Ohio,1982:693. |
[3] | J.O.Nilson .[J].Materials Science and Technology,1992,8:685. |
[4] | R.N.Gun.Duplex America 2000[M].Houston,USA,2000:299-314. |
[5] | L.Karlsson;L.Bengtsson;U.Rolander;S.Pak.[A].Stockholm,Sweden,1992:335-344. |
[6] | S.Hertzman;B.Lehtinen;E.Symniotis-Barradal.[A].Stockholm,Sweden,1992:345-359. |
[7] | G.S.Reis;A.M.Jorge Jr;O.Balancin .[J].Materials Research,2000,3(02):31. |
[8] | J.W.Pugh;J.O.Niebest .[J].Transactions AIME,1950,168:268. |
[9] | S.S.M.Tavares;V.F.Terra;J.M.Pardal;M.P.Cin-dra Fonseca .[J].Journal of Materials Science,2005,40:145. |
[10] | Y. S. Ahn;J. P. Kang .Effect of aging treatments on microstructure and impact properties of tungsten substituted 2205 duplex stainless steel[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2000(4):382-388. |
[11] | M.E.Wilms;V.J.Gadgil;J.M.Krougman;B.H.Kloster .[J].Materials at High Temperatures,1991,3:160. |
[12] | S.B.Kim;K.W.Paik;Y.G.Kim .[J].Materials Science and Engineering,1998,A247:67. |
[13] | L.Duprez;B.D.Cooman;N.Akdut .[J].Steel Research International,2000,10:417. |
[14] | T.H.Chen;K.L.Weng;J.R.Yang .[J].Materials Science and Engineering,2002,A338:259. |
[15] | E.M.L.E.M.Jackson;P.E.Devisser;L.A.Cornish .[J].Materials Characterization,1993,31:185. |
[16] | E.Evangelista;H.J.McQueen;M.Niewczas;M.Cabibbo .[J].Can Metal Quart,2004,43(03):339. |
[17] | Y.Maehara;N.Fujino;T.Kunitake .[J].Transactions of the Iron and Steel Institute of Japan,1983,23:247. |
[18] | Y.Maehara;M.Koike;N.Fujino;T.Kunitake .[J].Transactions of the Iron and Steel Institute of Japan,1983,23:224. |
[19] | J.Barcik;B.Brycka .[J].Metai Sci,1983,17:256. |
[20] | Y.Maehara;M.Koike;N.Fujino;T.Kunitake .[J].Transactions of the Iron and Steel Institute of Japan,1983,23(03):240-246. |
[21] | I.Calliari;M.Zanesco;E.Ramous .[J].Journal of Materials Science,2006,41:7643. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%