以天然鳞片石墨为原料,用改进的Hummers法制备氧化石墨。超声分散制备氧化石墨烯溶液,通过加入不同量的水合肼调节溶液的pH值,再通过水热法热还原,制备了在水中稳定分散的石墨烯溶液。利用扫描电子显微镜（SEM）、高分辨透射电镜（HR-TEM）、拉曼光谱（Raman）、原子力显微镜（AFM）、X射线衍射分析（XRD）、zeta电位及光学显微镜对制备的样品进行了表征,研究了不同温度、pH值对石墨烯溶液稳定性的影响。
A improved Hummers method was employed to prepare graphite oxide using natural flake graphite as raw materials. The graphene oxide solution was prepared by ultrasonic dispersion, and the pH value of solution was changed through adding different volume fraction of hydrazine hydrate. After hydrothermal reduction in au- toclave, stable dispersion graphene solutions were obtained. The as prepared samples were characterized by X- ray diffraction, scanning electron microscopy, transmission electron microscopy, Raman spectroscopy, atomic force microscope, zeta potential and optical microscope. The influence of temperature and pH value of the sta- bility of graphene solutions was investigated.
参考文献
| [1] | Park, S;Ruoff, RS .Chemical methods for the production of graphenes[J].Nature nanotechnology,2009(4):217-224. |
| [2] | Stankovich S;Dikin DA;Dommett GHB;Kohlhaas KM;Zimney EJ;Stach EA;Piner RD;Nguyen ST;Ruoff RS .Graphene-based composite materials[J].Nature,2006(7100):282-286. |
| [3] | Changgu Lee;Xiaoding Wei;Jeffrey W. Kysar;James Hone .Measurement of the Elastic Properties and Intrinsic Strength of Monolayer Graphene[J].Science,2008(5887):385-388. |
| [4] | Nair RR;Blake P;Grigorenko AN;Novoselov KS;Booth TJ;Stauber T;Peres NM;Geim AK .Fine structure constant defines visual transparency of graphene.[J].Science,2008(5881):1308-1308. |
| [5] | Zhang Y;Small J P;Pontius W V et al.Fabrication and electric-field-dependent transport measurements of macro- scopic graphite devices[J].Applied Physics Letters,2005,86(07):1-3. |
| [6] | Zhang Y;Tan Y W;Stormer H L et al.Experimental ob- servation of the quantum Hall effect and Berry's phase in graphene[J].Nature,2005,438:201-204. |
| [7] | Novoselov K S;Geim A K;Morozov S V et al.Electric field effect in atomically thin carbon films[J].Science,2004,306(5296):666-669. |
| [8] | Li Xiaolin;Zhang Guangyu;Bai Xuedong.Highly conducting graphene sheets and Longmuir Blodgett films[J].Nature Nanotechnology,2008(03):538-542. |
| [9] | Hass J;Millan-Otoya J E;First P N et al.Interface struc- ture of epitaxial graphene grown on 4H-SiC(0001)[J].Plays Rev B,2008,78:205424-205410. |
| [10] | Gamo Y.;Wakabayashi M.;Terai M.;Oshima C.;Nagashima A. .ATOMIC STRUCTURE OF MONOLAYER GRAPHITE FORMED ON NI(111)[J].Surface Science: A Journal Devoted to the Physics and Chemistry of Interfaces,1997(1/3):61-64. |
| [11] | Jinming Cai;Pascal Ruffieux;Rached Jaafar;Marco Bieri;Thomas Braun;Stephan Blankenburg;Matthias Muoth;Ari P. Seitsonen;Moussa Saleh;Xinliang Feng;Klaus Muellen;Roman Fasel .Atomically precise bottom-up fabrication of graphene nanoribbons[J].Nature,2010(Jul.22 TN.7305):470-473. |
| [12] | Choucair, M;Thordarson, P;Stride, JA .Gram-scale production of graphene based on solvothermal synthesis and sonication[J].Nature nanotechnology,2009(1):30-33. |
| [13] | K. S. Subrahmanyam;L. S. Panchakarla;A. Govindaraj .Simple Method of Preparing Graphene Flakes by an Arc-Discharge Method[J].The journal of physical chemistry, C. Nanomaterials and interfaces,2009(11):4257-4259. |
| [14] | Liying Jiao;Li Zhang;Xinran Wang;Georgi Diankov;Hongjie Dai .Narrow Graphene Nanoribbons From Carbon Nanotubes[J].Nature,2009(7240):877-880. |
| [15] | 杨勇辉,孙红娟,彭同江.石墨烯的氧化还原法制备及结构表征[J].无机化学学报,2010(11):2083-2090. |
| [16] | Lotya, M;Hernandez, Y;King, PJ;Smith, RJ;Nicolosi, V;Karlsson, LS;Blighe, FM;De, S;Wang, ZM;McGovern, IT;Duesberg, GS;Coleman, JN .Liquid Phase Production of Graphene by Exfoliation of Graphite in Surfactant/Water Solutions[J].Journal of the American Chemical Society,2009(10):3611-3620. |
| [17] | Hernandez Y;Nicolosi V;Lotya M;Blighe FM;Sun ZY;De S;McGovern IT;Holland B;Byrne M;Gun'ko YK .High-yield production of graphene by liquid-phase exfoliation of graphite[J].Nature nanotechnology,2008(9):563-568. |
| [18] | Khan, U.;O'Neill, A.;Lotya, M.;De, S.;Coleman, J.N. .High-concentration solvent exfoliation of graphene[J].Small,2010(7):864-871. |
| [19] | Hummers W S;Offeman R E .Preparation of graphitic oxide[J].Journal of the American Chemical Society,1958,80(06):1339. |
| [20] | Chen H C;Muller M B;Gilmore K J et al.Mechanically strong,electrically conductive and biocompatihle gra- phene paper[J].Advanced Materials,2008,20(18):3557-3561. |
| [21] | Meyer J C;Geim A K;Katsnelson M I et al.Thestructure of suspended graphene sheets[J].Nature,2007,446:60-63. |
| [22] | 王晓丹,周宁琳,汪炜燕,汤毅达,章峻,莫宏,沈健.羧基化氧化石墨烯-镧复合物抗凝血性能的研究[J].功能材料,2011(01):104-107. |
| [23] | Geim AK;Novoselov KS .The rise of graphene[J].Nature materials,2007(3):183-191. |
| [24] | 王延相,刘玉兰,王丽民,季敏霞,王成国.由聚丙烯腈基碳纤维制备石墨烯薄膜的探索研究[J].功能材料,2011(03):520-523. |
| [25] | Gupta A;Chen G;Joshi P;Tadigadapa S;Eklund PC .Raman scattering from high-frequency phonons in supported n-graphene layer films[J].Nano letters,2006(12):2667-2673. |
| [26] | Everett D H .Basic principles of colloid science[J].Royal Society of Chemistry,1989,338(6211):181-182. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%