采用电弧熔炼法制备了Fe81Ga19合金多晶样品,研究了不同热处理工艺对合金组织结构及磁致伸缩性能的影响.样品经过700℃、800℃和900℃保温后采用空冷、炉冷和淬火3种冷却方式.结果显示,经过不同热处理后样品的微观组织均为单相bcc结构,而磁致应变从34×10-8到94×10-6不等;当热处理温度为800℃时,淬火处理后可获得较好的磁致伸缩性能(88×10-6),而热处理温度较高(900℃)时,采用炉冷的方式可获得较好的磁致伸缩性能(94×10-6).推测热处理方式和晶体取向对Fe81Ga19合金磁致伸缩性能有较重要的影响.
Button ingots of polycrystalline Fe81Ga19 alloy are prepared by arc-melter, and the effects of different heat-treatments on their microstructure and magnetostriction are investigated. The specimens are annealed at 700℃, 800℃, and 900℃, and then cooled at different speeds, i.e. quenching into ice water, air cooling, or furnace cooling. The results show that specimens after different heat-treatments all exhibit single bcc structure, but the magnetostrictions vary from 34×10-6 to 94×10-6; When the heating ternpemture is 800℃, good rnagnetostriction (88×10-6) can be obtained by quenching. On the other hand, when the specimen is heated at a higher temperature (900℃), furnace cooling is a better way to get good magnetostrietion (94×10-6). It is speculated that the heat-treatment temperature and the crystal orientation may be two primary factors influencing the magentostriction of Fe81Ga19 alloy.
参考文献
| [1] | Guruswamy S.;Srisukhllmbowornchai N. .STRONG, DUCTILE, AND LOW-FIELD-MAGNETOSTRICTIVE ALLOYS BASED ON Fe-Ga[J].Scripta materialia,2000(3):239-244. |
| [2] | Extraordinary magnetoelasticity and lattice softening in bcc Fe-Ga alloys[J].Journal of Applied Physics,2003(10):8621-8623. |
| [3] | Zhang M C;Gao X X;Jiang H L et al.Effect of Ga content on the magnetostriction and microstructure of Fe-Ga ribbons[J].Journal of Alloys and Compounds,2007,431(1-2):42. |
| [4] | Clark A E.Mangnetostrictive Galfenol/Alfenol single crystalalloys under large compressive stresses[A].Brain,2000 |
| [5] | Clark A E.Magnetic and magnetostrictive properties of Galfenol alloys under large compressive stresses[A].Honolulu:The Japan Institute of Metals,2001:1711. |
| [6] | Srisukhumbowornchai N;Guruswamy S .Large magnetostriction in directionally solidified FeGa and FeGaAl alloys[J].Journal of Applied Physics,2001,90:5680. |
| [7] | 徐翔,蒋成保,徐惠彬.Fe72.5Ga27.5合金的相结构和磁致伸缩性能[J].金属学报,2005(05):483-486. |
| [8] | Hu C et al.Structural studies of decomposition in Fe-x at% Ga alloys[J].Journal of Alloys and Compounds,2008,465(1-2):244. |
| [9] | Clark A E;Wun-Fogle M;Restroff J B et al.Effect of quenching on the magnetostriction of Fe1-xGax[J].IEEE Transactions on Magnetics,2001,37(04):2678. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%