利用燃烧合成技术制备出单相柱状Ybα-SiAlON粉体,研究了原始配方对燃烧产物相组成和微观形貌的影响.结果表明:适量添加α-Si3N4能够减少团聚,有利于N2渗透和Si粉氮化,并可获得Yb α-SiAlON柱状晶.利用α-SiAlON作稀释剂,适量添加NH4F也可获得形态发育良好的Yb α-SiAlON柱状晶.过量添加α-Si3N4和NH4F则会造成反应前期α-Si3N4过剩而部分转化为β-Si3N4,最终导致β-SiAlON的形成.
参考文献
| [1] | Ekstrom T et al.[J].Journal of the American Ceramic Society,1992,75:259. |
| [2] | Hasan M .[J].Journal of the European Ceramic Society,1999,19:2349. |
| [3] | Chen I W;Rosenflanz A .[J].Nature,1997,389:701. |
| [4] | 刘光华 等.[J].稀有金属材料与工程,2003,32(zk):110. |
| [5] | Shen Z J et al.[J].Nature,2002,417:266. |
| [6] | Zenotchkine M.;Shuba R.;Chen IW. .Effect of seeding on the microstructure and mechanical properties of alpha-SiAlON: III, comparison of modifying cations[J].Journal of the American Ceramic Society,2003(7):1168-1175. |
| [7] | Zenotchkine M et al.[J].Journal of the American Ceramic Society,2001,84(07):1651. |
| [8] | Chen K X et al.[J].Journal of Materials Research,2001,16(07):1928. |
| [9] | Ferreira JMF et al.[J].Key Engineering Materials,2002,224-226:269. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%