通过观察显微组织、力学性能测试和利用三维取向分析术(ODF),研究了冷轧压下率对显微组织、力学性能、织构的影响.结果表明,随着冷轧压下率的升高,形变储能增加,退火后铁素体晶粒细小均匀,强度有所增加.变形织构{112} ＜110＞变弱,说明提高冷轧压下率可以消除变形织构,有利织构{111} ＜110＞增强,{001} ＜110＞变弱,共同提高rm值.当冷轧压下率为80％时,伸长率和rm达到峰值,同时△r较小,冲压性能最优.
参考文献
| [1] | 康永林.现代汽车板工艺及成形理论与技术[M].北京:冶金工业出版社,2009 |
| [2] | 郭艳辉,王昭东,李守卫,邹闻文.IF钢与ELC钢织构及性能的对比[J].东北大学学报（自然科学版）,2007(12):1713-1716. |
| [3] | P. Ghosh;C. Ghosh;R.K. Ray .Precipitation behavior and texture formation at different stages of processing in an interstitial free high strength steel[J].Scripta materialia,2008(3):276-278. |
| [4] | W.C. Jeong .Effect of hot-rolling temperature on microstructure and texture of an ultra-low carbon Ti-interstitial-free steel[J].Materials Letters,2008(1):91-94. |
| [5] | 李守华,李俊.汽车用高强度IF钢的研究进展[J].上海金属,2007(05):66-70. |
| [6] | Amit Kumar Gupta;D. Ravi Kumar .Formability of galvanized interstitial-free steel sheets[J].Journal of Materials Processing Technology,2006(2):225-237. |
| [7] | Bevis HUTCHINSON;Dorota ARTYMOWICZ .Mechanisms and Modelling of Microstructure/Texture Evolution in Interstitial-free Steel Sheets[J].ISIJ International,2001(6):533-541. |
| [8] | 吕庆功,陈光南,周家琮,唐历.深冲钢板的主要织构对塑性应变比的影响[J].钢铁研究,2000(05):40-43. |
| [9] | Yandong LIU,Chungang WANG,Qiwu JIANG,Tong HE,Liang ZUO.Individual Grain Orientation and Heterogeneous Deformation in Cold-deformed Interstitial-Free Sheet Steel[J].材料科学技术学报(英文版),2007(05):689-692. |
| [10] | 孙景宏 .微碳深冲钢板组织演变规律和工艺优化的研究[D].北京科技大学,2005. |
| [11] | Wang Z;Zhang P;Guo Y et al.Recrystallization texture characteristic and drawability of a warm rolled and cold rolled interstitial-free steel[J].Journal of Materials Engineering and Performance,2006,15(06):646-650. |
| [12] | 王先进;王作成;唐获 .成分及工艺对加磷高强IF钢成形性能的影响[J].钢铁,1993,28(03):34-38. |
| [13] | 刘战英,李晋霞,李艳娇,刘相华,王国栋.冷轧压下率分配对IF钢深冲性能的影响[J].河北理工学院学报,2003(04):29-37,44. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%