Structural and dielectric properties of polycrystalline samples of lead-free (1-x)(Na1/2Bi1/2)TiO3-xZnO, prepared using a high-temperature solid-state reaction method, are investigated in the composition range 0 ≤ x ≤ 0.10. Rietveld analyses of X-ray diffraction data indicated the formation of a single-phase hexagonal structure with R3c symmetry. Williamson-Hall approach was applied to estimate the apparent particle size and lattice strain of the compounds. Temperature dependence of dielectric constant showed that the addition of ZnO to (Na1/2Bi1/2)TiO3 shifts the phase transition temperature towards higher side, a property favourable for practical applications of these ceramics. Further, temperature dependent permittivity data provided low temperature coefficient of capacitance (TCC < 8%) up to 100°C. Furthermore, a decrease in the value of dielectric loss with an increase in ZnO content is observed.
参考文献
| [1] | K. Prasad, K. Kumari, Lily, K.P. Chandra, K.L. Yadav and S. Sen: Solid State Commun., 2007, 144, 42.[2 ] J. Kreisel and A.M. Glazer: Phys. Rev. B, 2001, 63, 174106.[3 ] S. Zhao, G. Li, T. Wang and Q. Yin: J. Phys. D-Appl. Phys., 2006, 39, 2277.[4 ] K. Miura and M. Tanaka: Jpn. J. Appl. Phys., 1996, 30, 2719.[5 ] D.J. Singh, M. Ghita, S.V. Halilov and M. Fornari: J. Phys. IV, 2005, 128, 47.[6 ] K. Prasad, K. Kumari, K.P. Chandra, K.L. Yadav and S. Sen: Mater. Sci.-Poland, 2009, 27, 373.[7 ] K. Kumari, K. Prasad, K.L. Yadav and S. Sen: Braz. J. Phys., 2009, 39, 297.[8 ] H. Nagata and T. Takenaka: J. Eur. Ceram. Soc., 2001, 21, 1299.[9 ] A. Herabut and A. Safari: J. Am. Ceram. Soc., 1997, 80, 2954.[10] X.X. Wang, H.L.W. Chan and C.L. Choy: Appl. Phys. A, 2005, 80, 333.[11] T. Takenaka and H. Nagata: Jpn. J. Appl. Phys., 1991, 30, 2236.[12] Y. Guo, K.I. Kakimoto and H. Ohsato: Mater. Lett., 2005, 59, 241.[13] Y.M. Li, W. Chen, J. Zhou, Q. Xu, X.Y. Gu and R.H. Liao: Physica B, 2005, 365, 76.[14] C.R. Zhou and X.Y. Liu: Bull. Mater. Sci., 2005, 30, 575.[15] C.R. Zhou and X.Y. Liu: J. Mater. Sci.: Mater. Electron., 2008, 19, 29.[16] X.Y. Liu, C.R. Zhou and Z.H. Shan: Bull. Mater. Sci., 2007, 30, 579.[17] M. Wu, Y. Lu and Y. Li: J. Am. Ceram Soc., 2007, 90, 3642.[18] Z. Yang, Y. Hou, B. Liu and L. Wei: Ceram. Int., 2009, 35, 1423.[19] T.S. Zhou, R.X. Huang, X.Z. Shang, F. Peng, J.Y. Guo, L.Y. Chai, H.S. Gu and Y.B. He: Appl. Phys. Lett., 2007, 90, 182903.[20] R.C. Chang, S.Y. Chu, Y.F. Lin, C.S. Hong and Y.P. Wong: J. Eur. Ceram. Soc., 2007, 27, 4453.[21] C.R. Zhou, X.Y. Liu, W.Z. Li and C.L. Yuan: Solid State Commun., 2009, 149, 481.[22] R. Zuo, C. Ye and X. Fang: J. Phys. Chem. Solids, 2008, 69, 230.[23] P. Marchet, E. Boucher, V. Dorcet and J.P. Mercurio: J. Eur. Ceram. Soc., 2006, 26, 3037.[24] H.H. Chung, C.F. Yang, K.H. Chen and C.C. Diao: Ferroelectrics, 2009, 385, 89.[25] X.X. Wang, H.L.W. Chan and C.L. Choy: J. Am. Ceram. Soc., 2003, 86, 1809.[26] J. Roisnel and J. Rodr{guez-Carvajal: WinPLOTR, Laboratoire Leon Brillouin (CEA-CNRS) Centre d'Etudes de Saclay: Gif sur Yvette Cedex, France, 2000.[27] J. Rodriguez-Carvajal: FullProf 2000: A Rietveld Refinement and Pattern Matching Analysis Program, Laboratoire Leon Brillouin (CEA-CNRS), France, 2001.[28] H.D. Megaw and C.N.W. Darlingtan: Acta Crystallogr. A, 1975, 31, 161.[29] L.B. McCusker, R.B. Von Dreele, D.E. Cox, D. Louer and P. Scardi: J. Appl. Cryst., 1999, 32, 36.[30] G.K. Williamson and W.H. Hall: Acta Metall., 1953, 1, 22.[31] K. Uchino and S. Nomura: Ferroelectr. Lett., 1982, 44, 55.[32] K. Prasad, R.N.P. Choudhary, S.N. Choudhary and R. Sati: Bull. Mater. Sci., 1996, 19, 505. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%