采用电子束蒸发技术在衬底温度为180℃条件下生长具有Ge覆盖层的非晶Si薄膜,并于500℃、600℃、700℃真空退火5h.采用Raman散射、X射线衍射(XRD)、全自动数字式显微镜等对所制备薄膜的晶化特性进行研究.结果表明,Ge覆盖层具有诱导非晶Si薄膜晶化的作用,且随着退火温度的升高a-Si薄膜晶化越显著.具有Ge覆盖层非晶薄膜经500℃退火5h沿Si(400)方向开始晶化,对应晶粒尺寸约为4.9 nm.将退火温度升高到700℃时,非晶硅薄膜几乎全部晶化,晶化多晶Si薄膜在Si(400)方向表现出很强的择优取向特性,晶粒尺寸高达23.3μm.与相同条件下制备的无Ge覆盖层的非晶Si薄膜相比,晶化温度降低了300℃.
参考文献
| [1] | Ulrich Wilhelm Paetzold;Wendi Zhang;Michael Prompers .Thin-film silicon solar cell development on imprint-textured glass substrates[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2013(9):617-622. |
| [2] | Yang H.;Wang H.;Chen GD.;Yu HC.;Xi JP. .A study of electrical uniformity for monolithic polycrystalline silicon solar cells[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,2002(3):407-412. |
| [3] | Boyce JB.;Lu JP.;Ho J.;Street RA.;van Schuylenbergh K.;Wang Y. .Pulsed laser crystallization of amorphous silicon for polysilicon flat panel imagers[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2002(Pt.2):731-735. |
| [4] | 潘永强.射频等离子体增强化学气相沉积SiNx薄膜的研究[J].光子学报,2007(06):1097-1101. |
| [5] | Park CD.;Cho MH.;Jan KJ.;Lee JY.;Kim HY. .Solid-phase crystallization of hydrogenated amorphous silicon/hydrogenated microcrystalline silicon bilayers deposited by plasma-enhanced chemical vapor deposition[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2000(2):268-274. |
| [6] | JIN Rui-min,LU Jing-xiao,LI Rui,WANG Hai-yan,FENG Tuan-hui.Solid-phase Crystallization of Amorphous Silicon Films by Rapid Thermal Annealing[J].半导体光子学与技术(英文版),2005(01):37-39. |
| [7] | 翟小利,谭瑞琴,戴世勋,王维燕,黄金华,宋伟杰.铝诱导晶化制备多晶硅薄膜研究进展[J].材料导报,2012(21):148-152. |
| [8] | Kim DY;Gowtham M;Shim MS;Yi JS .Polycrystalline silicon thin film made by metal-induced crystallization[J].Materials science in semiconductor processing,2004(4/6):433-437. |
| [9] | 张良艳,林祖伦,祁康成,韦新颖.金属Ni诱导非晶硅薄膜晶化研究[J].电子器件,2010(01):10-12. |
| [10] | 戴永兵,邹雪城,徐重阳,李兴教,沈荷生,张志明.准分子激光诱导非晶硅晶化制备多晶硅薄膜晶体管[J].微电子学,2000(05):343-346. |
| [11] | 孙启利,邓书康,申兰先,胡志华,李德聪,晒旭霞,孟代义.单晶硅衬底上Ge填埋层低温应力诱导重结晶制备多晶硅薄膜[J].人工晶体学报,2013(06):1082-1086. |
| [12] | 吕菲,刘春香,杨洪星,赵权,于妍,赵秀玲.锗单晶片的碱性腐蚀特性分析[J].半导体技术,2007(11):967-969. |
| [13] | 段宝兴,杨银堂.利用Keating模型计算Si（1-χ）Geχ及非晶硅的拉曼频移[J].物理学报,2009(10):7114-7118. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%