为了探讨TiO2在高C3S熟料水化过程中的作用机制,分析了TiO2对水泥水化组成和抗压强度的影响,并借助微量量热法和熟料矿物的高分辨图像分析了熟料的早期水化与抗压强度之间的关系.结果发现:0.5％TiO2虽延缓熟料的初始水化,但缩短了诱导期,提高了3天抗压强度,而掺量超过2.0％后,熟料的诱导期变长和3天强度降低,即诱导期的长短会影响到强度的变化.此外,TiO2对C3S晶格缺陷增加的贡献并没有引起3天强度的提高.
参考文献
| [1] | Kolovos K;Tsivilis S;Kakali G .The effect of foreign ions on the reactivity of the CaO-SiO2-Al2O3-Fe2O3 System[J].Cement and Concrete Research,2002,32:463-469. |
| [2] | N.K.Katyal;R.Parkash .Influence of titania on the formation of tricalcium silicate[J].Cement and Concrete Research,1999(3):355-359. |
| [3] | Ahluwalia S.C;Mathur V.K.Thermal studies on the effect of some transition metal oxides on the kinetics of formation and stabilization of C2 S[A].France:Paris,1980:40-45. |
| [4] | Knofel D .The incorporation of TiO2 into the phases of Portland cement clinker[J].Zement-Kalk-Gips,1979,32(01):35-40. |
| [5] | 干祖德 .TiO2对波特兰水泥熟料和波特兰水泥某些性能的影响[J].水泥,1978,3:51-53. |
| [6] | Teoreanu I;Muntean M;Balusoiu H .Addition of titanium dioxide to Portland cement clinkers[J].cement,1987,1:497-404. |
| [7] | 刘晓存,李艳君,汝莉莉,刘晓亮.TiO2对阿利特-硫铝酸盐水泥性能影响的研究[J].水泥工程,2007(02):11-14. |
| [8] | 石妍,杨华美,王迎春,杨华全,李家正.高钛矿渣对水泥基复合材料性能的影响[J].新型建筑材料,2009(09):1-4. |
| [9] | MA Xianwei,CHEN Huxing,WANG Peiming.Effect of TiO_2 on the Formation of Clinker with High C_3S[J].武汉理工大学学报(材料科学版)(英文版),2009(05):830-833. |
| [10] | Taylor H.F.W.Cement chemistry[M].London:Tomas Telford Publishing,1997 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%