研究了以乙炔为基本原料，用Ｎ２做载流气体；以纳米钻颗粒为催化剂在７００～８００℃常压下纳米碳管的宏观量制备．粗产品中纳米碳管的含量接近５０％，而且纳米碳管缺陷很少，直而长，石墨化好．纳米碳管的形核过程是因为碳在催化剂表面分布不均匀造成的．纳米碳管的生长极限在１５ｍｉｎ左右，然后生长变得缓慢，纳米碳管的一般长度在５～３０μｍ．
Acetylene cracked under normal pressure at 700-800℃ with active nanoscale cobalt particles as catalyst and carbon nanotubes were prepared on a large scale. The final product rate was above 50wt% after 10min growth, and also defects were almost nonexistent. The lengthes of the carbon nanotubes ranged from 5 to 30μm. Non-well distributed carbon on catalyst surface accelerated the nucleating process. The growing time limitation was about 15min and then growing process became slow.
参考文献
| [1] | Lijima S. Nature(London). 1991. 354--356. [2] Kratschmer W, Lamb L D, Fostiropoulos K, et al. Nature, 1990. 347--354. [3] Zhang Y, Lijima S. Applied Physics Letters, 1999, 75: 3087--3091. [4] Li Y L, Yu Y D, Liang Y. J. Mater. Res., 1997, 12: 1678--1682. [5] Chibante L P F, Thess A, Alford J M, et al. J. Phys. Chem., 1997. 385--781. [6] Laplaze D, Bernier P, Journet C, et al. Synth. Met., 1997, 86: 2295--2299. [7] Laplaze D, Bernier P, Journet C, et al. J. Phys.III(france), 1997, 7: 463--469. [8] Yacaman M J, Yoshida M M, Rendon L, et al. Apl. Phys. Lett., 1994. 223--329. [9] Song X Y, Cao W, Ayers M R, et al. J. Mater. Res., 1994, 10: 251--257. [10] Rodriguez N M, Kim M S, Baker R T K. J. Phys. Chem., 1994, 98: 13108--13114. [11] Lvanov V, Fonseca A, Nagy J B, et al. Carbon, 1995, 33: 1727--1733. [12] Fonseca A, Hernadi K, Nagy J B, et al. J. Mol. Cat., 1995. 107--159. [13] Cheng H M, Li F, Su G, et al. Apl. Phys. Lett., 1998, 72: 3282--3289. [14] 朱宏伟, 慈立杰, 等. 新型碳材料. 2000, 15: 49--51. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%