以正辛烷为模板,将N-异丙基丙烯酰胺(NIPAM)引入苯乙烯(St)/γ-甲基丙烯酰氧基丙基三甲氧基硅烷(KH-570)的细乳液共聚体系,制备了温敏型有机-无机杂化纳米微胶囊.通过红外(FT-IR)、透射电镜(TEM),激光粒径分析仪(DLS)表征了纳米微胶囊的结构和形态；采用紫外可见分光光度计(UV)研究了纳米微胶囊在临界温度附近对甲酚红的载入行为,考察了NIPAM用量对纳米微胶囊渗透性的影响.结果表明,当NIPAM用量为0.4g时,制得的纳米微胶囊的形貌完整、粒径均一、分散性较好,平均粒径为167nm,胶囊壁厚为24nm.纳米微胶囊的渗透性随着NIPAM用量的增加而增强.
参考文献
| [1] | 代春丽,蒋伟,侯信.聚合物中空微球材料研究进展[J].高分子材料科学与工程,2012(01):163-167. |
| [2] | McDonald CJ.;Chaput AB.;Stevens CJ.;Bouck KJ. .Emulsion polymerization of voided particles by encapsulation of a nonsolvent[J].Macromolecules,2000(5):1593-1605. |
| [3] | Chearuil FN;Corrigan OI .Thermosensitivity and release from poly N-isopropylacrylamide-polylactide copolymers.[J].International Journal of Pharmaceutics,2009(1/2):21-30. |
| [4] | 田晓冬,前田宁.N-异丙基丙烯酰胺共聚物的合成及温敏性[J].高分子材料科学与工程,2010(04):29-32. |
| [5] | Yi, FP;Zheng, SX .Effect of hydrophobic polystyrene microphases on temperature-responsive behavior of poly(N-isopropylacrylamide) hydrogels[J].Polymer,2009(2):670-678. |
| [6] | Cao, ZH;Shan, GR .Synthesis of Polymeric Nanocapsules with a Crosslinked Shell through Interfacial Miniemulsion Polymerization[J].Journal of Polymer Science. Part A, Polymer Chemistry,2009(6):1522-1534. |
| [7] | 曹志海,崔勤敏,单国荣.N-异丙基丙烯酰胺对细乳液聚合制备纳米胶囊形态的影响[J].高分子学报,2007(12):1116-1120. |
| [8] | 卢琴芳,尚玥 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%