对自制直径为30 nm～40 nm,长径比10～15的针形纳米碳酸钙进行表面改性后,将其应用于聚氯乙烯(PVC)的改性研究中,考察了改性针形纳米碳酸钙/PVC复合材料的力学性能.与未填充的PVC相比,纳米碳酸钙填充量为2.69%(体积分数)时,复合材料的拉伸强度、冲击强度和断裂伸长率分别提高了5.7%、11.3%和33.7%.改性后的纳米碳酸钙与PVC之间的界面作用与未改性碳酸钙相比有所减弱.扫描电镜照片(SEM)显示,添加了改性针形碳酸钙的聚氯乙烯断裂为韧性断裂,冲击断面呈现明显的拉丝现象.
参考文献
| [1] | Argon A S;Cohen R E.[J].Polymer,2003(44):6013-6032. |
| [2] | Xie XL;Liu QX;Li RKY;Zhou XP;Zhang QX;Yu ZZ;Mai YW .Rheological and mechanical properties of PVC/CaCO3 nanocomposites prepared by in situ polymerization[J].Polymer: The International Journal for the Science and Technology of Polymers,2004(19):6665-6673. |
| [3] | 陈立新,唐玉生,胡晓兰,梁国正,曾志安.晶须改性聚合物的研究概况[J].中国塑料,2005(01):1-5. |
| [4] | 胡庆福,刘洪杰,刘润静,胡永琪,李津津,焦其帅.针状纳米级碳酸钙的工业生产与应用[J].化工进展,2006(03):337-339. |
| [5] | Turcsa' nyi B;Puka' nszky B;Tu″do″s F .[J].Journal of Materials Science Letters,1988,7:160-162. |
| [6] | Demje' n Z;Puka' nszky B;Nagy .[J].Composites Part A:Applied Science and Manufacturing,1998,29(03):323-329. |
| [7] | Zhang Q X;Yu Z Z;Xie X L et al.[J].Polymer,2004,45:5985-5994. |
| [8] | Nicolais L;Narkis D .[J].Polymer Engineering and Science,1971,11:194-199. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%