Synthesis of C_f/TiALl_3 Composite by Infiltration-In Situ Reaction

材料科学技术（英文）, 2009, 25(6): 803-806.

^1, , ^2, , ^3, , ^4, , ^5, , ^6,

1.School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

2.Research Academy of Science and Industry Technology, Harbin Institute of Technology, Harbin 150001, China

3.Analysis and Measurement Center, Harbin Institute of Technology, Harbin 150001, China

4.School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

5.School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

6.School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

Synthesis of C_f/TiALl_3 Composite by Infiltration-In Situ Reaction

Yanmei Liu ^1, , Ziyang Xiu ^2, , Yongliang Guo ^3, , Longtao Jiang ^4, , Wensu Yang ^5, , Gaohui Wu ^6,

1.School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

2.Research Academy of Science and Industry Technology, Harbin Institute of Technology, Harbin 150001, China

3.Analysis and Measurement Center, Harbin Institute of Technology, Harbin 150001, China

4.School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

5.School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

6.School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

Keywords： Composites

Infiltration-in situ reaction synthesis of C_f/TiAl_3 composite was investigated. The as-cast material was obtained by titanium particles, carbon fibers and pure aluminum. Titanium particles and carbon fibers were mixed and pressed to form a preform firstly, and then molten pure aluminum was pressed into the preform, subsequently, cooled rapidly. In situ reaction samples were obtained by heating the as-cast material from 600 to 1000℃ for 1 h. The microstructural evolution of in situ reaction samples was analyzed by scanning electron microscopy and energy dispersive X-ray. In addition, the phase composition of products was inspected by X-ray diffraction. Experimental results showed that the dominant product of TiAl_3 and a small amount of Al_4C_3 were formed at low temperature. While TiAl_3 was not stable at high temperature, along with its decrease, TiC phase became favorable. In the final products, TiAl_3, TiC and Al_4C_3 were detected. Thus, the in situ reaction for Ti-Al-C system composite proceeded a formed-decomposed- precipitated mechanism.

参考文献

[1]	Y.X. Li;J.D. Hu;H.Y. Wang;Z.X. Guo;A.N. Chumakov .Thermodynamic and lattice parameter calculation of TiC_x produced from Al-Ti-C powders by laser igniting self-propagating high-temperature synthesis[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1/2):235-239.
[2]	D. Hu;X. Wu;M.H. Loretto .Advances in optimisation of mechanical properties in cast TiAl alloys[J].Intermetallics,2005(9):914-919.
[3]	C.J. Hsu;C.Y. Chang;P.W. Kao .Al-Al_3Ti nanocomposites produced in situ by friction stir processing[J].Acta materialia,2006(19):5241-5249.
[4]	C. Colinet;A. Pasturel .Ab initio calculation of the formation energies of L1_2, D0_(22), D0_(23) and one dimensional long period structures in TiAl_3 compound[J].Intermetallics,2002(8):751-764.
[5]	P. CORTES;W.J. CANTWELL .The prediction of tensile failure in titanium-based thermoplastic fibre-metal laminates[J].Composites science and technology,2006(13):2306-2316.
[6]	C. Arvieu;J. P. Manaud;P. Chadeyron;J. M. Quenisset .The design of an ephemeral interfacial zone for titanium matrix composites[J].Composites, Part A. Applied science and manufacturing,1998(9-10):1193-1201.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Synthesis of C_f/TiALl_3 Composite by Infiltration-In Situ Reaction

参考文献