以聚乙二醇为表面活性剂辅助水热法制备了纳米NixZn1-xFe2O4(x=0.4、0.5、0.6、0.7)铁氧体,通过XRD、FESEM、TEM和PNA分析,研究了不同的Ni2+含量对Ni-Zn铁氧体的粒度、形貌及其电磁损耗特性的影响.结果表明,水热法制备的晶体具有良好的结晶度,Ni2+含量不会影响样品的形态和结构,样品颗粒呈类球形,粒径在20～30 nm,在1～ 18 GHz的测试条件下具有介电损耗与磁损耗.Ni-Zn铁氧体电磁损耗随Ni2+含量的增加先增大后减小,当Ni2+含量x=0.6时,晶体晶化更加完整,粒度更加细化,对小于14 GHz中低频微波电磁损耗能力更强,在3GHz处,磁滞损耗正切tanδm达到最大值为1.03,介电损耗正切tanδe在3 GHz、9.5 GHz分别达到0.052、0.057,具有一定的微波吸收能力.
参考文献
| [1] | Wang, JH;Liu, YC;Liu, DC;Yu, YW;Guo, FB.Effect of electromagnetic field strength on Ni0.35Zn0.65Fe2O4 as performed by combustion synthesis[J].Journal of Magnetism and Magnetic Materials,200921(21):3646-3649. |
| [2] | Kumar, Sanjeev;Kumar, Pankaj;Singh, Vaishali;Mandal, Uttam Kumar;Kotnala, Ravinder Kumar.Synthesis, characterization and magnetic properties of monodisperse Ni, Zn-ferrite nanocrystals[J].Journal of Magnetism and Magnetic Materials,2015:50-57. |
| [3] | Characterization And Magnetic Properties Of Nanocrystalline Nickel Ferrite Synthesized By Hydrothermal Method[J].Materials Letters,200913/14(13/14):1183-1184. |
| [4] | 张瑜;薛向欣.稀土氧化物对Ni-Zn铁氧体/泡沫铝吸波性能的影响[J].中国稀土学报,2009(4):528-532. |
| [5] | 张永刚;徐波;王树林;唐宏志.镍锌铁氧体纳米材料制备及其光催化性能研究[J].功能材料,2013(14):2010-2013. |
| [6] | 彭穗 .水热法制备镍锌铁氧体及性能表征[D].中南大学,2007. |
| [7] | 古映莹;彭穗;覃展;庄树新;宋丰轩.水热模板法制备的纳米微孔镍锌铁氧体[J].磁性材料及器件,2007(2):37-39. |
| [8] | 陈雪刚;叶瑛;程继鹏.电磁波吸收材料的研究进展[J].无机材料学报,2011(5):449-457. |
| [9] | 陈瑶瑶;沈俊海;孔卫秋;李良超.镍锌铁氧体/膨胀石墨/聚苯胺复合物的电磁损耗性能[J].无机化学学报,2015(2):243-252. |
| [10] | 庄稼;陈学平;迟燕华;刘燕梅.纳米Ni0.5Zn0.5Fe2O4铁氧体的制备及电磁损耗特性研究[J].功能材料,2006(1):43-46. |
| [11] | 唐培朵;杨祥;沈翔;吴癸丽.镍锌钴铁氧体的水热低温合成与高频电磁性能研究[J].材料导报,2009(20):48-51,61. |
| [12] | 孙杰;刘建华;李松梅.尖晶石型Ni0.8Zn0.2Fe2O4纳米晶体的制备及电磁性能研究[J].无机材料学报,2005(5):1077-1082. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%