目的:获得一种耐黄变的高防腐转化膜。方法将经KH791改性的KH560与阳离子型聚氨酯进行复合,之后加入无机盐,获得复合钝化液。将钝化液辊涂于镀锌板上成膜,对膜层进行交流阻抗测试和中性盐雾试验,研究添加的无机盐对膜层耐蚀性的影响,并推测出其反应机理。结果阳离子型聚氨酯复合膜的交流阻抗谱上出现了3个时间常数,且在48 h盐雾试验中腐蚀面积为未添加无机盐的复合膜的1/8。结论 KH560经改性后,分子交联度有所提高。添加无机盐形成的三层结构体系膜层更能阻挡腐蚀介质的入侵,抗腐蚀性能明显提高。

Objective To obtain highly corrosion-resistant coating with resistance to yellow conversion. Methods Composite passivating fluid was obtained by adding inorganic salts into the composite solution of KH560 modified by KH791 together with cat-ionic polyurethane. Ac impedance test and salt spray test were performed with the coating after the composite passivating liquid was rolled on the galvanized sheet. The influence of the inorganic salts added on the coating corrosion resistance was studied and its re-action mechanism was inferred. Results The ac impedance spectroscopy of the cationic polyurethane composite coating displayed three time constants and in the 48 h salt spray test the corrosion area was only 1/8 that of the composite coating without addition of inorganic salts. Conclusion The molecular cross-linking degree was improved after KH560 was modified and the three-layer mem-brane structure formed by inorganic salt addition could stop the invasion of corrosive medium more effectively, so that its corrosion resistance could be obviously improved.

参考文献

[1] 王康,黄红军,万国顺,蒋磊.聚氨酯泡沫材料的粘接性能研究[J].装备环境工程,2012(05):122-125.
[2] 郦向宇,朱建琴,戴文琪.合成革用脂肪族聚氨酯树脂的合成[J].聚氨酯工业,2011(05):37-39.
[3] FUENTE D de la;SIMANCAS J;MORCILLO M .Effect of Variable Amounts of Rust at the Steel/Paint Interface on the Behavior of Anticorrosive Paint Systems[J].Progress in Or-ganic Coating,2003,46(04):241-249.
[4] ZHU Y F;XIONG J P;TANG Y M et al.EIS Study on Fai-lure Process of Two Polyurethane Composite Coating[J].Progress in organic Coatings,2010,69(01):7-11.
[5] 邓芹英;刘岚;邓慧敏.波谱分析教程[M].北京:科学出版社,2005
[6] YANG L X;LIU M X;LEI X L et al.Study on the Adsorp-tion Behavior ofγ-GPS on Low Carbon Steel Surfaces Using RA-IR,EIS and AFM[J].Applied Surface Science,2011,257(23):9895-9903.
[7] Xueming Wang;Guoli Li;Aiju Li;Zuoguang Zhang .Influence of thermal curing on the fabrication and properties of thin organosilane films coated on low carbon steel substrates[J].Journal of Materials Processing Technology,2007(1/3):259-264.
[8] 曾恩,张三平,周学杰,郑俊涛,周婵.热镀锌板表面硅烷处理耐蚀性能的研究[J].装备环境工程,2010(01):22-25.
[9] Lixia Yang;Jun Feng;Wenguang Zhang;Jun-e Qu .Film forming kinetics and reaction mechanism of γ-glycidoxypropyltrimethoxysilane on low carbon steel surfaces[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2010(22):6787-6794.
[10] 房振乾,陈群志,董兵,黄学军.飞机结构表面涂层体系改进研究[J].装备环境工程,2013(05):102-107.
[11] 赵静秋;王善琦 .用红外光谱法研究环氧树脂基体的固化特性[J].复合材料学报,1989,6(01):26-31.
[12] 张振海,叶鹏飞,徐丽萍,杨兴亮,张千峰.热镀锌板表面无机组分与有机硅烷复合钝化膜[J].表面技术,2013(02):14-17,33.
[13] Montemor M.F.;Simoes A.M. .The corrosion performance of organosilane based pre-treatments for coatings on galvanised steel[J].Progress in Organic Coatings: An International Review Journal,2000(1):17-26.
[14] 唐维学,张小琴,杨改霞.环境友好型铝合金表面钝化技术进展[J].腐蚀与防护,2010(04):272-275.
[15] 宫丽,卢燕平.热镀锌钢板钼酸盐钝化膜的改性及耐蚀性[J].钢铁研究学报,2007(03):88-92.
[16] INNOCENZI P;BRUSATIN G;GUGLIELMI M .3-glycid-oxypropyltrimethoxysilane-TiO2 Hybrid Organic-Inorganic Materials for Optical Limiting[J].Journal of Non-crystal-line Solids,2007,15(02):480-485.
[17] 张威,饶舟,徐恒志,黄毅平,许戈文.聚醚型阳离子水性聚氨酯的合成及性能研究[J].涂料技术与文摘,2011(03):25-28.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%