目的：快速研究大气环境对钢制输电铁塔腐蚀的影响。方法采用室内加速腐蚀实验，研究碳钢试样在湿度和 SO2浓度不同的气氛中的腐蚀行为。结果用极化曲线法测得的金属腐蚀速率与失重法测得的结果具有很高的一致性。相对湿度较低时，改变腐蚀性气体的浓度，对碳钢的腐蚀影响不显著；碳钢在高湿度的含 SO2气氛中会发生严重腐蚀。结论降低湿度是防止或减缓碳钢在含 SO2气氛中腐蚀的有效途径。
Objective To study the influence of atmospheric environment on steel transmission tower. Methods The corrosion behavior of carbon steel in different concentration of SO2 and different relative humidity was investigated using accelerated corrosion test. Results Severe corrosion occurred for carbon steel in SO2 environment with high relative humidity. Oxygen corrosion was the main corrosion type. The corrosion rate of carbon steel was greatly reduced in a low relative humidity environment. As the SO2 con-centration increased, the corrosion rate did not significantly increase. Conclusion Reducing relative humidity could effectively pre-vent or slow down the corrosion of carbon steel in SO2 environment.
参考文献
| [1] | 孙秋霞. 材料腐蚀与防护[M]. 北京:冶金工业出版社, 2001. SUN Qiu-xia. Corrosion and Protection of Materials [M]. Beijing:Metallurgical Industry Press,2001.,2001. |
| [2] | 叶堤,赵大为,李娟,张冬保,吕旭晨.大气污染对碳钢的腐蚀影响研究[J].重庆建筑大学学报,2005(01):80-83. |
| [3] | 梁彩凤.钢在中国大陆的大气腐蚀研究[J].电化学,2001(02):215-219. |
| [4] | 何建新,秦晓洲,易平,杨德模,李泽华,赖丽勤.Q235钢海洋大气腐蚀暴露试验研究[J].表面技术,2006(04):21-23. |
| [5] | 王晶晶,董士刚,叶美琪,金晓鸿,林昌健.环氧涂层室外暴晒和室内加速老化试验相关性研究[J].表面技术,2006(01):36-39. |
| [6] | 文邦伟,李继红.铝及铝合金在热带海洋地区大气腐蚀[J].表面技术,2004(06):21-23. |
| [7] | GB/T 9789-2008,金属和其他无机覆盖层通常凝露条件下的二氧化硫腐蚀实验[S]. GB/T 9789-2008,Metallic and Other Inorganic Coatings-Sulfur Dioxide Test with General Condensation of Moisture [S].,2008. |
| [8] | 汪川,王振尧,柯伟.Q235碳钢在SO2气体中的初期腐蚀行为[J].金属学报,2008(06):729-734. |
| [9] | ABDEL-REHIM S S,KHALED K F,ABD-ELSHAFI N S. Electrochemical Frequency Modulation as a New Technique for Monitoring Corrosion Inhibition of Iron in Acid Media by New Thiourea Derivation [J]. Electrochimica Acta,2006, 51:3269-3277.,2006. |
| [10] | AL-MOBARAK N A, KHALED K F, MOHAMED,et al. Employing Electrochemical Frequency Modulation for Stu-dying Corrosion and Corrosion Inhibitor of Copper in Sodium Chloride Solutions[J]. Arabian Journal of Chemistry,2011, 4:185-193.,2011. |
| [11] | DEFLOFIAN F,ROSSIA S,FEDRIZZI L,et al . EIS Study of Organic Coating on Zinc Surface Pretreated with Environ-mentally Friendly Products[J].Prog Org Coat,2005,52(4):271.,2005. |
| [12] | 王彬,苏艳.铝合金大气腐蚀行为及其防腐措施研究进展[J].装备环境工程,2012(02):64-68. |
| [13] | 郑利云,曹发和,刘文娟,陈安娜,廖晓宁,张鉴清.Q235钢在模拟自然环境下失效行为的电化学研究[J].装备环境工程,2011(04):8-15. |
| [14] | 王丽媛,王秀通,孙好芬,侯保荣.大气环境中SO2影响金属腐蚀的研究进展[J].装备环境工程,2011(02):62-66. |
| [15] | TSURU T, TAMIYA K I, NISHIKATA A. Formation and Growth of Micro-droplets during the Initial Stage of Atmos-pheric Corrosion [J]. Electrochimica Acta, 2004(49):2709-2715.,2004. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%