4Cr16MoN钢是一种新型钢种,它的平衡相图和CCT曲线可以为试验钢的大生产和热处理提供依据,为了和4Cr16Mo钢进行对比,通过J-Matpro模拟软件计算4Cr16MoN和4Cr16Mo钢的平衡相图,再利用DIL805A热膨胀相变仪测定其CCT曲线,试验条件是1050℃奥氏体化,保温5 min,按照10、3、1.2、1、0.5、0.1、0.08、0.05、0.03℃/S等不同冷速冷却.试验结果表明:在两种试验钢计算的平衡相图中,高温区很宽的温度范围内保持单相奥氏体,未出现δ铁索体相;两种试验钢CCT曲线都有独立的珠光体和贝氏体转变区域,4Cr16MoN钢的P临界冷速和B临界冷速分别是0.1℃/s和1.2℃/s,而4Cr16Mo钢的P临界冷速和B临界冷速分别小于0.03℃/s和3℃/s.
参考文献
| [1] | Reinhold Schneider,Klaus Sammt,Roland Rabitsch,Michael Haspel.Heat Treatment and Properties of Nitrogen Alloyed, Martensitic, Corrosion-resistant Steels[J].材料热处理学报,2004(05):582-587. |
| [2] | Perko J;Redl C;Leitner H .Influence of Heat Treatment on the Microstructure and Toughness of B(O)HLER M333 Isoplast Steel[J].La Metallurgia Italiana,2009,4:1. |
| [3] | Kaluba W J;Kaluba T;Taillard R .The Austenitizing Behavior of High-Nitrogen Martensitic Stainless Steels[J].Scripta Materialia,1999,41(12):1289. |
| [4] | Leda H.Nitrogen in Martensitic Stainless Steels[J].Journal of Materials Processing Technology,1995(53):263. |
| [5] | 曹建春,雍岐龙,刘清友,孙新军.含铌钼钢中微合金碳氮化物沉淀析出及其强化机制[J].材料热处理学报,2006(05):51-55. |
| [6] | Prokoshkina, V;Kaputkina, L.Peculiarities of martensitic transformations and martensite structure in high nitrogen steels[J].Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008:762-765. |
| [7] | 胡湘红.9Ni钢固态相变规律探讨[J].宽厚板,2007(06):33-39. |
| [8] | 刘宗昌,闫俊萍,赵莉萍,王贵,李强,田玉新.23MnNiCrMo钢的相变及组织特征[J].包头钢铁学院学报,2001(01):30-33. |
| [9] | 赵宝纯,李桂艳,柳永浩,杨静,黄磊.含Mo低碳微合金钢CCT曲线的测定与分析[J].热加工工艺,2008(22):37-39. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%