采用自组装方法，在铜合金表面首先制备了6-（3-三乙氧基硅基丙基）氨-1，3，5-三嗪-2，4-二硫醇单钠盐（TES）自组装薄膜，然后用正辛基三甲氧基硅烷（OTES）或十六烷基三甲氧基硅烷（HDTMS）对TES修饰的铜合金表面进行硅烷化处理，得到了具有疏水功能的复合自组装薄膜。通过傅里叶变换红外光谱（FT—IR）、接触角、循环伏安、极化曲线和扫描电子显微镜（SEM）对铜合金表面的自组装薄膜进行了表征。结果表明，与未处理的铜合金相比，经复合自组装薄膜修饰的铜合金表面接触角由89．4°上升到123．7°，提高了铜合金表面的疏水性；FT—IR表明了复合自组装薄膜在铜合金表面的形成；SEM测定结果表明该方法成功地在铜合金表面获得均匀致密的有机硅烷复合膜；循环伏安及极化曲线测试均表明了该复合膜有效地提高了铜合金的耐腐蚀能力。
6-(3-triethoxysilylpropyl) amino-l, 3, 5-triazine-2, 4-dithiol monosodium (TES), octyltriethoxysilane (OTES) and hexadecyltrimethoxysilane (HDTMS) were used to prepare single and complex self-assembled films on copper alloy surface. The films were characterized by means of FT-IR spectrum, contact angle measurement, cyclic voltammogram, polarization curve and scanning electron microscopy (SEM). The results show that the contact angle of the copper alloy surface covered with complex film is up to 123.7° compared with 89.4° of bare copper. FT-IR spectra verifies the formation of complex self- assembled film on the copper surface. Cyclic voltammogram and polarization curves suggest that the corrosion resistance performance of the complex film is better than that of the single TES selbassembled film, and the protection efficiency is up to 96.54%.
参考文献
| [1] | 余向飞.铜及其合金缓蚀剂的研究进展[J].材料开发与应用,2010(03):106-109. |
| [2] | 马洪芳.铜表面自组装缓蚀功能膜的电化学研究[J].山东建筑大学学报,2009(04):299-302. |
| [3] | 岳艳枝,桑商斌,唐爱东,伍秋美,赵林梅.对羟基苯甲酸自组装膜对铜的缓蚀作用[J].广州化工,2011(03):78-81. |
| [4] | Zhixin Kang;Qi Ye;Jing Sang;Yuanyuan Li .Fabrication of super-hydrophobic surface on copper surface by polymer plating[J].Journal of Materials Processing Technology,2009(9):4543-4547. |
| [5] | B. V. Appa Rao;Md. Yakub Iqbal;B. Sreedhar .Electrochemical and surface analytical studies of the self-assembled monolayer of 5-methoxy-2-(octadecylthio)benzimidazole in corrosion protection of copper[J].Electrochimica Acta,2010(3):620-631. |
| [6] | 康永,柴秀娟.有机高分子缓蚀剂的研究进展[J].中国井矿盐,2011(01):5-8. |
| [7] | 石新颖,田学雷.金属表面有机疏水涂层的研究进展[J].材料导报,2010(01):76-79. |
| [8] | Laibinis PE;Whitesides GM .Self-assembled monolayers of n- alkanethiolates on copper are barrier films that protect the rental against oxidation by air[J].American Chemical Society,1992,114:9022-9028. |
| [9] | Taira Y;Kamada K .Effects of primers containing sulfur and phosphate monomers on bonding type IV gold alloy.[J].Journal of dentistry,2008(8):595-599. |
| [10] | 王景刚,王芳,罗和义,王亚斌.铜表面复合超疏水薄膜的制备及表征[J].精细化工,2011(02):108-110,124. |
| [11] | Fang Wang;Yabin Wang et al.Preparation of 6-diallylamino-1,3,5-triazine-2,4-dithiol functional nanofilm by electrochemical polymerization technique on aluminum surface[J].International Journal of Electrochemical Science,2011,6:793-803. |
| [12] | Yamamota M;Suzuki M et al.Film formation from mixed solutions of 1,3,5-triazine-2,4-dithione and phosphate onto Au,Ag,and Cu suhstrates[J].Journal of Physical Chemistry C,2008,112(17):6914-6923. |
| [13] | F. Zucchi;V. Grassi;A. Frignani;G. Trabanelli .Inhibition of copper corrosion by silane coatings[J].Corrosion Science,2004(11):2853-2865. |
| [14] | F. Zucchi;A. Frignani;V. Grassi;G. Trabanelli;M. DalColle .The formation of a protective layer of 3-mercapto-propyl-trimethoxy-silane on copper[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(3):1570-1583. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%