采用等离子体电解氧化方法在铝合金表面制备了氧化锆涂层,电解液为包含Zr(OH)4颗粒的碱性溶液.涂层的组成、结构通过XRD、 EPMA进行了研究.结果显示,涂层主要由t-ZrO2、m-ZrO2、α-Al2O3和γ-Al2O3组成,t-ZrO2为涂层的主晶相,分布在涂层表面,而α-Al2O3出现在涂层的内侧.涂层表面呈颗粒状,颗粒尺寸约为1～2μm.在氧化过程中,Zr(OH)4颗粒在电场力的作用下向等离子体放电通道口沉积,在放电产生的高温作用下直接转化为氧化锆.
参考文献
| [1] | Koski K,Holsa J,Juliet P.Surf.Coat.Technol.,1999,120-121:303-312. |
| [2] | Boulouz M,Boulouz A,Giani A,et al.Thin Solid Films,1998,323:85-92. |
| [3] | Schmidt-Zhang P,Sandow K P,Adolf F,et al.Sensors and Actuators B:Chemical,2000,70 (1-3):25-29. |
| [4] | Pulker H K.Surf.Coat.Technol.,1999,112(1-3):250-256. |
| [5] | Matthews A,Young S J,Joseph M,et al.Surf.Coat.Technol.,1997,94-95:123-130. |
| [6] | Goto T.Surf.Coat.Technol.,2005,198(1-3):367-371. |
| [7] | Hembram K P S S,Dutta G,Waghmare U V,et al.Physica B:Condensed Matter,2007,399(1):21-26. |
| [8] | 辛世刚,宋力昕,赵荣根,等(XIN Shi-Gang,et al).无机材料学报(Journal of Inorganic Materials),2006,21(2):493-498. |
| [9] | Yerokhin A L,Nie X,Leyland A,et al.Surf.Coat.Technol.,1999,122:73-93. |
| [10] | Rudnev V S,Morozova V P,Yarivaya T P,et al.Prot.Met.,1999,35(5):524-530. |
| [11] | 许煜汾,范文元.中国粉体技术,2000,(6):251-253. |
| [12] | Ji Z,Haynes J A,Ferber M K,et al.Surf.Coat.Technol.,2001,135 (2-3):109-117. |
| [13] | Kih J S,Marzouk H A,Reucroft P J.Thin Solid Films,1995,254:33-38. |
| [14] | Xin S G,Song L X,Zhao R G,et al.Thin Solid Films,2006,515:326-332. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%