以Q235钢作为基体材料,采用喷涂的方法制备了耐温耐磨聚酰胺酰亚胺(PAI)涂层材料.利用MMW-1型万能摩擦磨损试验机研究了SiC及聚四氟乙烯(PTFE)含量对PAI涂层摩擦学性能的影响,同时对PAI涂层进行了TG热性能分析.结果表明:当SiC含量为10％(质量分数)、PTFE含量为0.8％(质量分数)时,PAI涂层摩擦学性能达到最优;TG曲线表明制备的PAI涂层热失质量温度在350℃以上;PAI涂层在250℃保温1h后,表面无气泡、剥落及裂纹等缺陷.
参考文献
| [1] | JOST H P .Developing situation and tendency of the tribological research[J].JOURNAL OF JAPANESE SOCIETY OF TRIBOLOGISTS,1992,37:2-10. |
| [2] | Mori Y.;Shindo H.;Yamazaki M. .Film designed for lubricative coated steel sheets[J].Progress in Organic Coatings: An International Review Journal,2000(1/4):119-120. |
| [3] | 乔红斌,郭强.高分子固体润滑耐磨涂层研究进展[J].机械工程材料,2004(02):1-3,23. |
| [4] | 张利,律微波,王绪科,张新恩,李金辉,王林,张荣军.固体润滑高分子涂层材料研究进展[J].新技术新工艺,2010(02):53-55. |
| [5] | Huseyin Unal;Mehmet Kurt;Abdullah Mimaroglu .Tribological performance of industrial polyamide-imide and its composite under different cooling conditions[J].Journal of polymer engineering,2012(3):201-206. |
| [6] | Yoshikawa M;Guiver MD;Robertson GP .Molecularly imprinted films derived from Torlono (R) polyamide-imide[J].Journal of Molecular Structure,2005(1/3):41-46. |
| [7] | YANG C P;LIN J H .Preparation and properties of aromatic polyamides and polyimides derived from 3,3-bis[4-(4-aminophenoxy) phenyl]phthalide[J].Polym Sci Part A:Polym Chem,1994,32(03):423-433. |
| [8] | 宋晓峰,黄志荣,李庆敏.聚酰胺-酰亚胺树脂自润滑复合涂料的研制及性能[J].材料保护,2013(03):18-21. |
| [9] | 中国科学院兰州化学物理研究所 .常温固化防锈干膜润滑剂[P].中国,CN95103904.0,1995-04-07. |
| [10] | 刘家浚.材料磨损原理及其耐磨性[M].北京:清华大学出版社,1993 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%