研究了等温热处理的共沉淀MgO(10.4mol%)-ZrO2粉体的酸浸滤,并利用XRD和TEM表征了粉体的物相和晶粒尺寸.结果表明:在1450℃,MgO全部溶入ZrO2晶格,相应的相是四方和立方相;在1350-750℃,只有约2.2mol%MgO溶入ZrO2晶格,相应的相为四方相;750℃以下,溶入ZrO2晶格的MgO反而增加,在500℃时,固溶度为7.7mol%MgO,相应的相是立方相.其余的MgO分布在ZrO2晶粒的表面.

MgO(10.4mol%)-ZrO2 powders coprecipitated were heated isothermally and quenched from 500 to 1450℃, then acid-leached and milled. Afterwards, the prepared powders were characterized by XRD and TEM technologies. The results show that all MgO(10.4mol%) is almost soluble in ZrO2 after isothermal heating at 1450℃ for 2h and quenching; at 750-1350℃, the solubility of MgO is about 2.2mol%; at 500℃, it is 7.7mol%. The rest of MgO exists on the surface of the ZrO2 crystallites.

参考文献

[1] Hannink R H J, Kelly P M, Muddle B C. J. Am. Ceram. Soc., 2000, 83 (3): 461--487.
[2] Readey M J, Lee R R, Halloran J W, et al. J. Am. Ceram. Soc., 1990, 73 (6): 1499--1503.
[3] Brett N H, Gonzalez M, Bouillot J, et al. J. Mater. Sci., 1984, 19 (4): 1349--1358.
[4] Livage J, Doi K, Mazieres C. J. Am. Ceram. Soc., 1968, 51 (6): 349--353.
[5] Zhou Y, Lei T. Q, Liu G B, et al. J. Chinese Ceram. Soc., 1988, 16 (1): 27--33.
[6] Du Y, Jin Z P, Huang P Y. Phase Equilibria Diagrams-Phase Diagrams for Ceramics, 1991, Vol. Ⅺ, Fig. 9250: 98.
[7] Viechnicki D, Stubican V S. J. Am. Ceram. Soc., 1965, 48 (6): 292--297.
[8] Duwez P, Odell F, Brown Jr F H. J. Am. Ceram. Soc., 1952, 35 (5): 107--113.
[9] Duran P, Rodriguez J M, Recio P. J. Mater. Sci., 1991, 26 (2): 467--472.
[10] Stubican V S. Adv. Ceram., 1988, 24A [Sci. Technol. Zirconia 3]: 71--82.
[11] Sim S M, Stubican V S. J. Am. Ceram. Soc., 1987, 70 (7): 521--526.
[12] Grain C T. J. Am. Ceram. Soc., 1967, 50 (6): 288--290.
[13] Rong T-J, Huang X-X, Wang S-W, et al. J. Am. Ceram. Soc., (MS:187604 C)
[14] Garvie R C. J. Phy. Chem., 1965, 69 (4): 1238--1243.
[15] Garvie R C, Nicholson P S. J. Am. Ceram. Soc., 1972, 55 (6): 303--305.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%