采用腐蚀挂片和电化学试验研究了20号钢在不同Cl-浓度的高矿化度溶液中的腐蚀行为.结果表明,20号钢在高矿化度条件下不利于硫酸盐还原菌(SRB)的繁殖,在高浓度盐溶液中微生物腐蚀倾向低,钢的表面未产生微生物膜,以全面腐蚀为主.在低浓度的盐溶液中发生微生物腐蚀倾向大,且能形成不连续的、分布不均匀的微生物膜.
参考文献
| [1] | 张小里,陈志昕,刘海洪,郭生武,陈开勋.环境因素对硫酸盐还原菌生长的影响[J].中国腐蚀与防护学报,2000(04):224-229. |
| [2] | 赵海,李安明,万波,刘克鑫.一株中度嗜盐硫酸盐还原菌的分离及生理特性研究[J].应用与环境生物学报,1995(01):61-67. |
| [3] | SALVAREZZA R C;VIDELLA H A;ARVIA A J .The electrochemical behaviour of mild steel in phosphate-borate-sulphide solutions[J].Corrosion Science,1983,23:717-732. |
| [4] | SALVAREZZA R C;VIDELLA H A .Passivity breakdown of mild steelin seawaterin the presence of sulfate reducing bacterial[J].CORROSION,1980,36:550-554. |
| [5] | RINGAS C;ROBOINSON F P A .Corrosion of stainless steel by SULFATE-reducing bacteria-electrochemical techniques[J].CORROSION,1988,44:386-396. |
| [6] | D. Starosvetsky;O. Khaselev;J. Starosvetsky;R. Armon;J. Yahalom .Effect of iron exposure in SRB media on pitting initiation[J].Corrosion Science,2000(2):345-359. |
| [7] | POSTGATE J R.The sulphate-reducing bacteria[M].Cambridge:Cambridge University Press,1984 |
| [8] | GB/T16545-1996.金属和合金的腐蚀腐蚀试样上腐蚀产物的清除[S]. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%