采用现代仪器测试和恒电流充放等电化学测试手段,对包覆修饰石墨微观结构与嵌锂电化学进行分析.扫描电子显微镜(SEM)、红外光谱仪(FTIR)和X射线衍射仪(X-ray)测试表明,热处理工艺使得石墨微晶尺寸增大,微晶的有序度提高,d002值变大,同时包覆修饰使得石墨微粒表面形成包覆炭层,石墨表面钝化.电化学测试表明,包覆修饰减弱了充放电过程中不可逆分解反应,使锂在石墨中的嵌入电位得到改善,石墨负极中固相锂离子的扩散系数适度增大.
参考文献
| [1] | Masaki Yoshio;Hongyu Wang;Kenji Fukuda;Yoichiro Hara;Yoshio Adachi .Effect of CarbonCoating onElectrochemical Performance of Treated Natural Graphite as Lithium-Ion Battery Anode Material[J].Journal of the Electrochemical Society,2000(4):1245-1250. |
| [2] | Yoon S H;Kim H;Seung M O .Surface modification of graphite by coke coating for reduction of initial irreversible capacity in lithium secondary batteries[J].Journal of Power Sources,2001,94:68. |
| [3] | 仇卫华,张刚,卢世刚.锂离子电池负极材料--树脂包覆石墨的性能[J].电源技术,1999(01):7. |
| [4] | 俞政洪,吴锋.锂离子电池炭负极材料的研究--包覆对天然石墨容量衰减的影响[J].新型炭材料,2002(04):29-32,37. |
| [5] | W. b. Xing;R. A. Dunlap;J. R. Dahn .Studies of lithium insertion in ballmilled sugar carbons[J].Journal of the Electrochemical Society,1998(1):62-70. |
| [6] | 马树华.锂离子电池负极碳材料的表面改性与修饰Ⅱ.具有“核壳”结构的碳及其对电池性能的影响[J].电化学,1997(01):86. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%