利用焊接粗晶区连续冷却淬火方法,对比分析了钛处理钢和普通C-Mn钢焊接粗晶区连续冷却不同阶段的相变组织,研究了铁素体相变规律.结果表明,C-Mn钢焊接粗晶区主要为晶界铁素体+魏氏组织铁素体;钛处理钢焊接粗晶区主要为晶界铁素体+魏氏组织铁素体+晶内铁素体组织.在钛处理钢中,晶界铁素体、魏氏组织铁素体和晶内铁素体的相变开始温度相同,但各自长大的动力学条件不同.当晶内铁素体和魏氏组织铁索体竞争发生相变时,晶内铁素体在晶内弥散分布氧化物夹杂上的非均质形核抑制了魏氏组织铁素体向晶内的长大.
参考文献
| [1] | Svensson L E .Microstructure and Impact Toughness and Strength of Weld HAZ[J].Welding Journal,1990,69(12):454. |
| [2] | Thewlis G .Transformation Kinetics of Ferrous Weld Metals[J].Materials Science and Technology,1994,10(04):110. |
| [3] | Homma H;Okita S;Matsuda S et al.Improvement of HAZ Toughness in HSLA Steel by Introducing Finely Dispersed Tioxide[J].Welding Journal,1987,66:301. |
| [4] | Byun J S;Shim H H;Cho Y W .Non-Metallic Inclusion and Intragranular Nucleation of Ferrite in Ti-Killed C-Mn Steel[J].Acta Materialia,2003,51:1593. |
| [5] | Rees G I;Bhadeshia H K D H .Thermodynamics of Acicular Ferrite Nucleation[J].Materials Science and Technology,1994,10:353. |
| [6] | Thewlis G;Whiteman JA;Senogles DJ .Dynamics of austenite to ferrite phase transformation in ferrous weld metals[J].Materials Science and Technology: MST: A publication of the Institute of Metals,1997(3):257-274. |
| [7] | Shim J H;Oh Y J;Suh J Y .Ferrite Nucleation Potency of Non-Metallic Inclusions in Medium Carbon Steels[J].Acta Materialia,2001,49:2115. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%