At room temperature, the rolling treatment of steel-mushy Al-7graphite bonding plate was carried out under different relative reduction. The influence of rolling on interfacial mechanical property of this bonding plate was studied. The results show that, for steel-mushy Al-7graphite bonding plate which is made up of 1.2 mm in thickness 08Al steel plate and 2.0 mm in thickness Al-7graphite layer, there is a nonlinear relationship between interfacial shear strength of bonding plate and relative reduction of rolling. When relative reduction of rolling is smaller than 2.59%, with the increasing of relative reduction, interfacial shear strength of bonding plate increases gradually. When relative reduction of rolling is bigger than 2.59%, with the increasing of relative reduction, interfacial shear strength of bonding plate decreases continuously. When relative reduction of rolling is 2.59%, the largest interfacial shear strength 77.0 MPa can be obtained.

参考文献

[1] PengZHANGandYunhuiDU .[J].Journal of Materials Science and Technology,2000,17(02):224.
[2] PengZHANG;YunhuiDU .[J].Transaction of nonferrous metal society,2001,11(02):239.
[3] ShixianLI.[M].Graphite, Chemistry Industry Press, Beijing,1991:11.
[4] FKenneth.Metal Base Composite Material[M].北京:国防工业出版社,1982:45.
[5] PengZHANGandYunhuiDU .[J].Journal of University of Science and Technology Beijing(English Edition),2001,8(03):203.
[6] PengZHANGandYunhuiDU .[J].Journal of University of Science and Technology Beijing(English Edition),2001,8(04):283.
[7] GuangZHANG .[J].Chin Journal of Mater Research,1997,11(06):649.
[8] ZhongzeCUI.Metallurgy and Heat Treatment[M].北京:机械工业出版社,1989:145.
[9] QinHUA;Feipeng QI .[J].Materials for Mechanical Engineering,1995,19(01):32.
[10] TKomatsu .[J].Japanese Journal of Metal,1981,45:416.
[11] ZhiyeZHAO.Plastic Forming of Metal[M].北京:冶金工业出版社,1987:58.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%