综合搅拌铸造法和原位反应制备了Al2O3颗粒增强Al-4Mg基复合材料，并对制备的Al-4Mg基复合材料进行了透射电镜（TEM）观察分析，发现Al2O3/Al之间不存在固定的位向关系。但存在如下优先的位向关系：( )Al2O3//(111) Al，[ ]Al2O3//[ ] Al，[ ]Al2O3//[ ] Al。
Al2O3 particles, in situ decomposed from Al2(SO4)3, reinforced Al--4Mg matrix composites were made through stir casting. Al2O3/Al interface in the Al--4Mg matrix composites was studied by transmission electron microscopy (TEM). The measurements of crystallographic orientation relationship between Al2O3 and Al at Al2O3/Al interface show that no fixed and unique orientation relationship existed, though the following preferential ones were observed: ：( )Al2O3//(111) Al，[ ]Al2O3//[ ] Al，[ ]Al2O3//[ ] Al。