以E-44环氧树脂改性水性聚氨酯为基料,三聚氰胺、季戊四醇为阻燃剂,制备了一种阻燃涂料.测试了该涂料的附着力、耐水性、吸水率、阻燃性及热失重.结果表明,改性后涂料的涂膜附着力达到1级,耐水时间为240 h,吸水率16.5%,阻燃时间可达10 min以上,耐高温及阻燃性能明显提高.
参考文献
| [1] | 耿耀宗.现代水性涂料:工艺@配方@应用[M].北京:中国石化出版社,2003:1-165. |
| [2] | CHEN S A;CHAN W C .Polyurethane cationomers (1):structure-property relationships[J].Journal of Polymer Science:Part B,1998,28(09):1499-1514. |
| [3] | Kim BK.;Lee JC. .MODIFICATION OF WATERBORNE POLYURETHANES BY ACRYLATE INCORPORATIONS[J].Journal of Applied Polymer Science,1995(7):1117-1124. |
| [4] | Jeong Saw Lee;Byung Kyu Kim .Modification of Aqueous Polyurethanes via Latex AB Crosslinked Polymers[J].Journal of Applied Polymer Science,2001(6):1315-1322. |
| [5] | DIETERICH D .Aqueous emulsions,dispersions and solutions of polyurethanes:synthesis and properties[J].Progress in Organic Coatings,1981,9(03):281-340. |
| [6] | 王春会,李树材.环氧树脂改性水性聚氨酯的合成与性能研究[J].聚氨酯工业,2005(06):20-23. |
| [7] | 马庆麟.涂料工业手册[M].北京:化学工业出版社,2001:1121-1122. |
| [8] | 肖忠平,陆继圣,马世春,杨文斌.热重法研究阻燃杉木间伐材热解反应动力学[J].福建林学院学报,2002(02):113-116. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%