金属在海洋中的腐蚀受C1-浓度和溶液中溶解氧含量的影响,以往的研究多为低C1-浓度下的腐蚀,对于高C1-浓度及与溶解氧含量相关的研究较少.为此,采用动电位扫描和电化学阻抗谱(EIS)方法,研究了船用903钢在不同NaC1浓度溶液及薄液膜中的腐蚀规律,探讨了C1-浓度变化过程中溶解氧含量对903钢腐蚀的影响.结果表明:903钢在NaC1溶液及薄液膜中的腐蚀规律是不同的,初期随C1-浓度的升高,溶液中的腐蚀速率先升高后降低,而在薄液膜中腐蚀速率一直升高;相同C1-浓度下,薄液膜中的溶解氧含量高于溶液中的溶解氧含量,其腐蚀速率比溶液中的高.腐蚀规律不同的主要原因是溶解氧含量不同.
The corrosion behavior of 903 steel in solution of NaCl containing various Cl- concentrations and thin film electrolyte was evaluated by means of polarization scanning and electro-chemical impedance spectroscopy.The effect of dissoloved oxygen was investigated. Results show that the 903 steel has different corrosion behaviors in solution of NaCl and thin film electrolyte.Namely, at the early stage of test, the corrosion rate of the steel in solution of NaCl increased to a maximum and then decreased along with increasing content of NaCl, but the corrosion rate in thin film electrolyte increased monotonically with increasing con-tent of NaCl. Besides, under the same concentration of Cl-, the dissolved oxygen content in the thin film electrolyte was higher than that in the solution of NaCl, and the steal had a higher cor-rosion rate in the former than in the latter. This was mainly attrib-uted to the different contents of dissolved oxygen in the two cases.
参考文献
| [1] | 林翠,王凤平,李晓刚.大气腐蚀研究方法进展[J].中国腐蚀与防护学报,2004(04):249-256. |
| [2] | 陈新华,董俊华,韩恩厚,柯伟.干湿交替环境下Cu、Mn合金化对低合金钢腐蚀行为的影响[J].材料保护,2007(10):19-22. |
| [3] | Nishimura T.;Katayama H. .Electrochemical Behavior of Rust Formed on Carbon Steel in a Wet/Dry Environment Containing Chloride Ions[J].Corrosion: The Journal of Science and Engineering,2000(9):935-941. |
| [4] | 黄建中;左禹.材料的耐蚀性和腐蚀数据[M].北京:化学工业出版社,2003:93-95. |
| [5] | 胡茂圃.腐蚀电化学[M].北京:冶金工业出版社,1991:220-225. |
| [6] | 徐乃欣;张承典;丁翠红 .加速大气腐蚀试验的一个新方案[J].中国腐蚀与防护学报,1990,10(03):228-232. |
| [7] | 张学元,柯克,杜元龙.金属在薄层液膜下电化学腐蚀电池的设计[J].中国腐蚀与防护学报,2001(02):117-122. |
| [8] | 安百刚,张学元,韩恩厚,李洪锡.Zn在模拟酸雨溶液中及其液膜下的腐蚀[J].金属学报,2004(02):202-206. |
| [9] | 柯伟;杨武.腐蚀科学技术的应用和失效案例[M].北京:化学工业出版社,2002:261-270. |
| [10] | Leygraf C;Graedel T;韩恩厚.大气腐蚀[M].北京:化学工业出版社,2005:226-234. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%